Cohesive demineralized bone compositions
Demineralized bone matrix fibers and a demineralized bone matrix composition are provided. The demineralized bone matrix fibers have an average fiber length in the range from about 250 μm to about 2 mm and an aspect ratio of greater than about 4. The demineralized bone matrix composition includes demineralized bone matrix fibers and a biocompatible liquid in an amount to produce a coherent, formable mass. The formable mass retains its cohesiveness when immersed in a liquid. Methods for making the demineralized bone matrix fibers and composition are also provided.
1. A demineralized bone matrix composition comprising:
fibers of demineralized bone matrix consisting of fiber lengths between 250 μm to 2 mm and an aspect ratio of greater than about 4; and
a biocompatible liquid in an amount to produce a coherent, formable mass.
2. The composition of claim 1 , wherein the demineralized bone matrix fibers have an average thickness in the range from about 50 μm to about 250 μm.
3. The composition of claim 1 , wherein the aspect ratio of said fibers is greater than about 10.
4. The composition of claim 1 , wherein the aspect ratio of said fibers is in a range from about 10 to about 50.
5. The composition of claim 1 , wherein the demineralized bone matrix fibers have an average width to average thickness ratio of less than about 5.
6. The composition of claim 1 , wherein the biocompatible liquid is selected from the group consisting of water, saline, buffer solution, serum, bone marrow aspirant, blood, platelet-rich plasma, and mixtures thereof.
7. The composition of claim 1 , further comprising particles of demineralized bone matrix having an aspect ratio of less than about 3.
8. The composition of claim 1 , wherein the composition further comprises an osteoinductive additive.
9. The composition of claim 8 , wherein the osteoinductive additive is selected from the group consisting of bone marrow aspirant, blood, blood products, synthetic and naturally-derived bone morphogenic proteins, growth factors, particulate demineralized bone matrix, and mixtures thereof.
10. The composition of claim 1 , wherein the composition further comprises an osteoconductive additive.
11. The composition of claim 10 , wherein the osteoconductive additive is selected from the group consisting of calcium phosphates, collagen, collagen-derivatives, calcium sulfate, particulate demineralized bone matrix, naturally-derived allogenic bone mineral, and naturally-derived autogenic bone mineral.
12. The composition of claim 1 , wherein the composition further comprises an additive that modifies the handling characteristics of the composition.
13. The composition of claim 12 , wherein the additive at least partially coats the demineralized bone fibers.
14. The composition of claim 12 , wherein the additive is selected from the group consisting of gelatin, carboxymethyl cellulose, hydroxypropyl methylcellulose, methylcellulose, hydroxyethyl cellulose, cellulose derivatives, alginate, hyaluronic acid, sodium salts, polyvinyl pyrrolidones, polyvinyl alcohol, arabic gum, guar gum, xantham gum, chitosans, and poloxamers.
15. The composition of claim 1 , wherein the relative amounts of demineralized bone matrix fibers and biocompatible liquid range from about 1:10 to about 10:1 wt/wt.
16. The composition of claim 1 , wherein the relative amounts of demineralized bone matrix fibers and biocompatible liquid range from about 1:4 to about 4:1 wt/wt.
17. The composition of claim 1 , wherein the relative amount of demineralized bone matrix fibers and biocompatible liquid is about 1:1 wt/wt.
18. The composition of claim 1 , wherein the demineralized bone matrix fibers are obtained from cortical autogenic, cortical allogenic, cortical xenogeneic, cancellous autogenic, cancellous allogenic, cancellous xenogeneic, corticocancellous autogenic, corticocancellous allogenic, or corticocancellous xenogeneic bone.
19. The composition of claim 1 , wherein the composition has a consistency such that it is injectable through an 18-gauge needle.
20. A demineralized bone matrix composition comprising:
(a) a dry component comprising fibers of demineralized bone matrix consisting of fiber lengths between 250 μm to 2 mm and an aspect ratio of greater than about 4, wherein said demineralized bone matrix fibers are present in an amount greater than 40 wt % of said dry component, and
(b) a biocompatible liquid in an amount to produce a coherent formable mass.
21. The composition of claim 20 , wherein the demineralized bone matrix fibers have an average thickness in the range from about 50 μm to about 250 μm.
22. The composition of claim 20 , wherein the demineralized bone matrix fibers have an aspect ratio greater than about 10.
23. The composition of claim 20 , wherein the demineralized bone matrix fibers have an average width to average thickness ratio of less than about 5.
24. The composition of claim 20 , further comprising an additive selected from the group consisting of osteoconductive additives, osteoinductive additives, and additives that modify the handling characteristics of the composition.
25. A demineralized bone matrix fiber composition, comprising:
a collection of fibers of demineralized bone matrix of which at least 25 wt % between 250 μm to 2 mm and an aspect ratio of greater than about 4.
26. The composition of claim 25 , wherein at least 50 wt % of the demineralized bone matrix fibers have between 250 μm to 2 mm and an aspect ratio of greater than about 4.
27. The composition of claim 25 , wherein at least about 75 wt % of the demineralized bone matrix fibers have fiber lengths between 250 μm to 2 mm and an aspect ratio of greater than about 4.
28. The composition of claim 25 , wherein the demineralized bone matrix fibers have an average thickness in the range from about 50 μm to about 250 μm.
29. The composition of claim 25 , wherein the demineralized bone matrix fibers have an average width to average thickness ratio of less than about 5.
30. The composition of claim 25 , further comprising an additive selected from the group consisting of osteoinductive additives, osteoconductive additives, and additives that modify the handling characteristics of the composition.
31. A preformed demineralized bone matrix article having a predetermined shape, said article comprising:
fibers of demineralized bone matrix having consisting of fiber lengths between 250 μm to 2 mm and an aspect ratio of greater than about 4; and
a biocompatible liquid in an amount to produce a coherent, formable mass.
32. The article of claim 31 , wherein said article has a density in the range of about 0.3 g/cc to about 0.7 g/cc.
33. The article of claim 31 , wherein said article has a compression strength greater than about 10 MPa.
34. A method for making a demineralized bone matrix composition, comprising:
combining fibers of demineralized bone matrix, having consisting of fiber lengths between 250 μm to 2 mm and an aspect ratio of greater than about 4, and an amount of a biocompatible liquid to produce a coherent, formable mass.
35. A method of making a preformed demineralized bone matrix article having a predetermined shape comprising:
combining fibers of demineralized bone matrix having consisting of fiber lengths between 250 μm to 2 mm and an aspect ratio of greater than about 4, and an amount of a biocompatible liquid to produce a coherent, formable mass;
forming the mass into a preformed article having the predetermined shape; and
drying the preformed article.
36. The method of claim 35 , wherein the preformed article is lyophilized.
37. The method of claim 36 , wherein the preformed article has a density of about 0.3 g/cc.
38. The method of claim 35 , wherein the preformed article is oven dried.
39. The method of claim 38 , wherein the preformed article has a density of about 0.7 g/cc.