Thrust needle roller bearing, support structure receiving thrust load of compressor for car air-conditioner, support structure receiving thrust load of automatic transmission, support structure for continuously variable transmission, and support structure receivin
A thrust needle roller bearing has a washer formed of a thin steel plate and needle rollers, at least said washer has a nitrogen enriched layer at a surface layer portion, amount of retained austenite in said surface layer portion is at least 5 volume % and at most 25 volume %, and austenite grain number of said surface layer portion is 11 or higher. Thus, a long life thrust needle roller bearing resistant to an early failure caused by surface damage such as surface-originated flaking and also resistant to common, load dependent rolling contact fatigue can be provided.
1. A thrust needle roller bearing having a washer formed of a thin steel plate and a needle roller, wherein at least said washer has a nitrogen enriched layer at a surface layer portion, an average amount of retained austenite in said surface layer portion is at least 8.2 volume % and at most 22.0 volume %, and austenite grain size number defined by Japanese Industrial Standard of said surface layer portion is 11 or higher.
2. The thrust needle roller bearing according to claim 1 , wherein nitrogen content of said surface layer portion is in the range of 0.1 mass % to 0.7 mass %.
3. A support structure receiving thrust load of a compressor for a car air-conditioner in which a swash plate rotates as a main shaft rotates and a piston swings accordingly, including
a thrust needle roller bearing receiving thrust load generated by the rotation of said swash plate, having a washer formed of a thin steel plate and a needle roller, wherein at least said washer has a nitrogen enriched layer at a surface layer portion, an average amount of retained austenite in said surface layer portion is at least 8.2 volume % and at most 22.0 volume %, and austenite grain size number defined by Japanese Industrial Standard of said surface layer portion is 11 or higher.
4. The support structure receiving thrust load of a compressor for a car air-conditioner according to claim 3 , wherein nitrogen content of said surface layer portion is in the range of 0.1 mass % to 0.7 mass %.
5. A support structure receiving thrust load of an automatic transmission including a torque converter having an impeller and a turbine opposite to each other with a stator in between, comprising
a thrust needle roller bearing having a washer formed of a thin steel plate and a needle roller, at least between said stator and said impeller or between said stator and said turbine, wherein
at least said washer has a nitrogen enriched layer at a surface layer portion, an average amount of retained austenite in said surface layer portion is at least 8.2 volume % and at most 22.0 volume %, and austenite grain size number defined by Japanese Industrial Standard of said surface layer portion is 11 or higher.
6. The support structure receiving thrust load of an automatic transmission according to claim 5 , wherein nitrogen content of said surface layer portion is in the range of 0.1 mass % to 0.7 mass %.
7. A support structure for a continuously variable transmission in which rotation of an input shaft is changed in a nonstep manner and transmitted to an output shaft, including
a thrust needle roller bearing receiving thrust load generated by the rotation either of said input shaft or said output shaft, having a washer formed of a thin steel plate and a needle roller, wherein at least said washer has a nitrogen enriched layer at a surface layer portion, an average amount of retained austenite in said surface layer portion is at least 8.2 volume % and at most 22.0 volume %, and austenite grain size number defined by Japanese Industrial Standard of said surface layer portion is 11 or higher.
8. The support structure for a continuously variable transmission according to claim 7 , wherein nitrogen content of said surface layer portion is in the range of 0.1 mass % to 0.7 mass %.
9. A support structure receiving thrust load of a manual transmission allowing, by engagement between a gear of an input shaft and a gear of a counter shaft and engagement between a gear of the counter shaft and a gear of an output shaft, stepwise change of speed of rotation of said output shaft from the speed of rotation of said input shaft, including
a thrust needle roller bearing receiving thrust load of any of said input shaft, said counter shaft and said output shaft, having a washer formed of a thin steel plate and a needle roller, wherein at least said washer has a nitrogen enriched layer at a surface layer portion, an average amount of retained austenite in said surface layer portion is at least 8.2 volume % and at most 22.0 volume %, and austenite grain size number defined by Japanese Industrial Standard of said surface layer portion is 11 or higher.
10. The support structure receiving thrust load of a manual transmission according to claim 9 , wherein nitrogen content of said surface layer portion is in the range of 0.1 mass % to 0.7 mass %.