Piezoelectric film laminate and method of manufacturing the same
A piezoelectric film laminate including a sapphire substrate and a lead zirconate titanate niobate film and a potassium niobate film formed on the sapphire substrate.
1. A method of manufacturing a piezoelectric film laminate, comprising:
providing a sapphire substrate;
providing a precursor composition including a precursor for forming a lead zirconate titanate niobate film, the precursor including at least lead, niobium, titanium, and zirconium and having a partial ester bond;
applying the precursor composition to the sapphire substrate and heating the applied precursor composition to form a lead zirconate titanate niobate film; and
forming a potassium niobate film on the lead zirconate titanate niobate film.
2. The method of manufacturing a piezoelectric film laminate as defined in claim 1 , wherein the precursor is dissolved or dispersed in an organic solvent.
3. The method of manufacturing a piezoelectric film laminate as defined in claim 2 , wherein the organic solvent is an alcohol.
4. The method of manufacturing a piezoelectric film laminate as defined in claim 1 ,
wherein the precursor composition is obtained by mixing a sol-gel raw material including a hydrolysis-condensation product of a metal alkoxide of at least niobium, titanium, and zirconium, a polycarboxylic acid or a polycarboxylic acid ester, and an organic solvent; and
wherein the precursor composition includes the precursor having an ester bond resulting from esterification of the polycarboxylic acid or a polycarboxylic acid derived from the polycarboxylic acid ester and the metal alkoxide.
5. The method of manufacturing a piezoelectric film laminate as defined in claim 4 , wherein the polycarboxylic acid or the polycarboxylic acid ester is a dicarboxylic acid or a dicarboxylic acid ester.
6. The method of manufacturing a piezoelectric film laminate as defined in claim 5 , wherein the dicarboxylic acid ester is at least one ester selected from a succinic acid ester, a maleic acid ester, and a malonic acid ester.
7. The method of manufacturing a piezoelectric film laminate as defined in claim 4 , wherein the sol-gel raw material further includes a metal carboxylate.
8. The method of manufacturing a piezoelectric film laminate as defined in claim 7 , wherein the metal carboxylate is a lead carboxylate.