Method for manufacturing plated film, cathode roll for plating, and method for manufacturing circuit board
View Patent ↗A method for manufacturing a plated film by bringing a film having a conductive surface into electrical contact with a cathode roll with a liquid film interposed between the film and the cathode and forming a metal plating on the conductive surface of the film, characterized in that the relation E 0 >[(I/Cs)×d]/σ where E 0 is the reduction potential of the metal forming the plating, I is the value of the current flowing through the cathode roll for plating, Cs is the area of the conductive surface of the film in electrical contact with the cathode roll with a liquid film interposed therebetween, d is the thickness of the gap between the cathode roll and the conductive film, and σ is the conductivity of the liquid forming the liquid film present in the gap. A cathode roll having a surface roughness Rmax of 1 μm or less is also disclosed. Further a cathode roll having a Vickers hardness of the surface of 200 or more is disclosed.
1. A method for producing a plated film, comprising the steps of: carrying a resin film having a conductive surface into a plating solution accommodated in a plating bath provided with an anode,
passing the resin film through the plating solution and,
carrying the resin film from the plating bath to run along a cathode roll which is arranged outside and in the downstream side of the plating bath,
wherein the conductive surface of the resin film is brought into electrical contact with the cathode roll through an electrolyte layer for electroplating a plating layer on the conductive surface of the film, and
wherein the following relation is satisfied:
E 0 >[( I/Cs )× d]/σ
where E 0 is the reduction potential of a metal constituting the plating layer; I is the value of a current flowing through the cathode roll for plating; Cs is the area of the conductive surface of the resin film in electrical contact with the cathode roll through the electrolyte layer; d is the thickness of a gap between the cathode roll and the conductive surface of the resin film; and σ is the conductivity of a liquid constituting the electrolyte layer, and
further wherein the carrying tension T of the resin film is from 10 N/m to 320 N/m.
2. A method for producing a plated film, according to claim 1 , wherein the conductivity σ of the liquid constituting the electrolyte layer existing in the gap is controlled by means of the concentration of an electrolyte mainly composed of sulfuric acid.
3. A method for producing a plated film, according to claim 1 , wherein the conductivity σ of the liquid constituting the electrolyte layer existing in the gap is from 1 mS/cm to 100 mS/cm.
4. A method for producing a plated film, according to claim 1 , wherein the thickness d of the gap is from 20 μm to 500 μm.
5. A method for producing a plated film, according to claim 4 , wherein the thickness d of the gap is controlled by means of a carrying tension of the resin film.
6. A method for producing a plated film, according to claim 1 , wherein the plating layer is composed of copper.
7. A method for producing a plated film, according to claim 1 , wherein the resin film is made of a polyimide resin or polyester resin.
8. A method for producing a plated film according to claim 1 , wherein the electrolyte layer is supplied by a separate electrolyte accommodating pan.