Golf ball and process for preparing the same
The object of the present invention is to provide a golf ball which is excellent in abrasion-resistance, durability and resilience and a process for preparing the same. The gist of the present invention resides in using a cover composition having a thermoplastic polyurethane and a heat reactive microcapsule encapsulating a polyisocyanate; during the molding of the cover, the polyisocyanate is contained inside the microcapsule to inhibit the crosslinking reaction between the polyisocyanate and the thermoplastic polyurethane to maintain the moldability of the cover, while, after the molding of the cover, the golf ball body is heated in order to promote a crosslinking reaction between the polyisocyanate released from the microcapsule and the thermoplastic polyurethane to improve the abrasion-resistance, durability and resilience of the resultant urethane cover.
1. A golf ball comprising
a core, and
a cover containing a crosslinked polyurethane,
wherein the crosslinked polyurethane is formed by heating and reacting a cover composition comprising a thermoplastic polyurethane having a hydroxyl group and heat reactive microcapsules encapsulating a polyisocyanate, and
the heat reactive microcapsules have an outer shell comprising a thermoplastic resin having a softening point ranging from 80° C. to 250° C.
2. The golf ball according to claim 1 , wherein the heat reactive microcapsule releases the polyisocyanate by a heat treatment at a temperature of 160° C. to 200° C. for 3 minutes to 10 minutes.
3. The golf ball according to claim 1 , wherein the thermoplastic polyurethane has a functional group reactive with an isocyanate group.
4. The golf ball according to claim 1 , wherein the cover has a slab hardness of from 20D to 60D in shore D hardness.
5. The golf ball according to claim 1 , wherein the cover has a thickness of 2.0 mm or less.
6. A process for preparing a golf ball comprising the steps of:
molding a cover from a cover composition comprising a thermoplastic polyurethane and heat reactive microcapsules encapsulating a polyisocyanate to produce a golf ball body, and heating the golf ball body, thereby allowing a crosslinking reaction between the polyisocyanate of the heat reactive microcapsules and the thermoplastic polyurethane to produce a golf ball comprising a core and a cover containing a crosslinked polyurethane, wherein the heat reactive microcapsules have an outer shell comprising a thermoplastic resin having a softening point ranging from 80° C. to 250° C.
7. The process for preparing the golf ball according to claim 6 , wherein a thermoplastic polyurethane having a functional group reactive with an isocyanate group is used as the thermoplastic polyurethane.
8. The process for preparing the golf ball according to claim 6 , wherein the heating the golf ball body is conducted at a temperature of 70° C. or higher for 12 hours or more.
9. A process for preparing a golf ball having a core and a cover covering the core, comprising
providing a cover composition comprising a thermoplastic polyurethane and heat reactive microcapsules encapsulating a polyisocyanate,
molding the cover composition into a shell,
covering the core with at least two shells,
compression molding the core covered with at least two shells to prepare a golf ball body, and
heating the golf ball body, thereby allowing a crosslinking reaction between the polyisocyanate of the heat reactive microcapsules and the thermoplastic polyurethane to produce a golf ball comprising a core and a cover containing a crosslinked polyurethane, wherein the heat reactive microcapsules have an outer shell comprising a thermoplastic resin having a softening point ranging from 80° C. to 250° C.
10. The process for preparing the golf ball according to claim 9 , wherein molding the cover composition into the shell is conducted by a compression molding at the following conditions:
molding temperature ranging from 100° C. to 180° C.,
molding pressure ranging from 0.5 MPa to 25 MPa, and
molding time ranging from 1 minute to 30 minutes.
11. The process for preparing the golf ball according to claim 9 , wherein molding the cover composition into the shell is conducted by an injection molding at the following conditions:
molding temperature ranging from 100° C. to 250° C., and
molding pressure ranging from 3 MPa to 10 MPa.
12. The process for preparing the golf ball according to claim 9 , wherein compression molding the core covered with at least two shells is conducted at the following conditions:
molding temperature ranging from 100° C. to 180° C.,
molding pressure ranging from 0.5 MPa to 25 MPa, and
molding time ranging from 1 minute to 30 minutes.
13. The process for preparing the golf ball according to claim 9 , wherein heating the golf ball body is conducted at the following conditions:
heating temperature ranging from 70° C. to 130° C., and
heating time ranging from 12 hours to 168 hours.
14. The process for preparing the golf ball according to claim 9 , wherein heating the golf ball body is conducted at the following conditions:
heating temperature ranging from 70° C. to 90° C., and
heating time ranging from 30 hours to 168 hours.
15. The process for preparing the golf ball according to claim 9 , wherein heating the golf ball body is conducted at the following conditions:
heating temperature ranging from 110° C. to 130° C., and
heating time ranging from 12 hours to 40 hours.
16. The process for preparing the golf ball according to claim 9 , wherein the heat reactive microcapsules release the polyisocyanate by a heat treatment at a temperature of 160° C. to 200° C. for 3 minutes to 10 minutes.
17. The process for preparing the golf ball according to claim 9 , wherein the heat reactive microcapsules have an outer shell comprising a thermoplastic resin having a softening point ranging from 80° C. to 250° C.
18. The process for preparing the golf ball according to claim 9 , wherein a thermoplastic polyurethane having a functional group reactive with an isocyanate group is used as the thermoplastic polyurethane.
19. A process for preparing a golf ball having a core and a cover covering the core, comprising
providing a cover composition comprising a thermoplastic polyurethane and heat reactive microcapsules encapsulating a polyisocyanate,
injection-molding the cover composition onto the core to prepare a golf ball body, and heating the golf ball body, thereby allowing a crosslinking reaction between the polyisocyanate of the heat reactive microcapsules and the thermoplastic polyurethane to produce a golf ball comprising a core and a cover containing a crosslinked polyurethane, wherein the heat reactive microcapsules have an outer shell comprising a thermoplastic resin having a softening point ranging from 80° C. to 250° C.