Soft polymer compositions having improved high temperature properties
Disclosed are soft polymer compositions comprising an ethylene/alkyl (meth)acrylate copolymer and a crystalline polyolefin, such as polypropylene homopolymers or polypropylene copolymers, wherein the ethylene/alkyl (meth)acrylate copolymer has a higher melt viscosity than the polyolefin. Also disclosed are such compositions modified by materials that improve the scratch-and-mar properties of the blends, the preparation and use of these compositions in such processes as extrusion and injection molding, and articles made from these compositions.
1. A composition comprising a blend and optionally a second component wherein
the blend comprises 20 to 50 weight % of at least one crystalline polyolefin and 50 to 80 weight % of at least one ethylene/alkyl (meth)acrylate copolymer, the ethylene/alkyl (meth)acrylate copolymer is selected solely from the group consisting of ethylene/methyl acrylate copolymer, ethylene/ethyl acrylate copolymer, ethylene/butyl acrylate copolymer, and combinations of two or more thereof;
the ratio of the melt viscosity of the ethylene/alkyl (meth)acrylate copolymer to the melt viscosity of the polyolefin is greater than 1.25:1; and
the second component includes plasticizer, stabilizer, antioxidant, UV absorber, antistatic agent, dye, pigment or other coloring agent, fluorescent whitening agent, inorganic filler, delustrant, terminating agent, fire-retardant, lubricant, reinforcing agent, foaming or blowing agent, processing aid, slip additive, antiblock agent, release agent, tackifying resin, or combinations of two or more thereof.
2. The composition of claim 1 wherein the blend comprises 25 to 45 weight % of the polypropylene including polypropylene homopolymer or polypropylene copolymer and 55 to 75 weight % of the ethylene/alkyl-(meth)acrylate copolymer.
3. The composition of claim 2 wherein the ratio of the melt viscosity of the ethylene/alkyl (meth)acrylate copolymer to the melt viscosity of the propylene is greater than 1.5.
4. The composition of claim 2 wherein the composition has a Vicat temperature of at least 60° C.
5. The composition of claim 3 wherein the composition has a Vicat temperature of at least 65° C.
6. The composition of claim 2 wherein the alkyl (meth)acrylate is present in the ethylene/alkyl (meth)acrylate copolymer in a range from about 5 to about 40 weight %.
7. The composition of claim 4 wherein the alkyl (meth)acrylate is present in said ethylene/alkyl (meth)acrylate copolymer in a range from about 10 to about 35 weight %.
8. The composition of claim 5 wherein the alkyl (meth)acrylate is present in said ethylene/alkyl (meth)acrylate copolymer in a range from about 10 to about 35 weight %.
9. The composition of claim 6 wherein the ethylene/alkyl (meth)acrylate is a tubular reactor produced copolymer.
10. The composition of claim 8 wherein the ethylene/alkyl (meth)acrylate is a tubular reactor produced copolymer.