Method of thermal spraying
An adhesion strength of spray coating comparable to that obtained in a conventional combination of blast treatment and gas flame spraying can be realized even if roughening is conducted with the use of simple tools by performing in advance such a roughening treatment that the average roughness (Ra) of the surface of the thermal spray subject falls within the range of 2 to 10 μm with the use of a grinding tool, and thereafter carrying out thermal spraying under such conditions that the average area of each of molten particles when molten particles of a thermal spray material have stuck to the surface of thermal spray subject falls within the range of 10000 to 100000 μm 2 . In the roughening by grinding tools, a large-scale apparatus is not needed as different from the blast treatment, and portable small tools can be used in overhead location work at field repair. The scattering of powder resulting from grinding is slight so that the danger of environmental pollution is low.
1. A plasma spraying method of spraying a metal thermal spray material onto a metal body to form a spray coating for corrosion prevention, said plasma spraying method comprising:
roughening a surface of the metal body by using a grinding tool to achieve an average roughness Ra of the surface in a range of 2 μm to 10 μm; and
performing plasma spraying in a manner such that an average area covered by each molten particle of the metal thermal spray material when the molten particles have stuck to the surface of the metal body is 10000 μm 2 to 100000 μm 2 to thereby form the spray coating.
2. The plasma spraying method according to claim 1 , wherein said performing plasma spraying comprises using a plasma spraying apparatus which uses the metal thermal spray material in the form of a wire.
3. The plasma spraying method according to claim 2 , further comprising performing a sealing treatment on the spray coating after said performing plasma spraying.
4. The plasma spraying method according to claim 2 , wherein the metal thermal spray material is aluminum or an aluminum alloy.
5. The plasma spraying method according to claim 4 , further comprising performing a sealing treatment on the spray coating after said performing plasma spraying.
6. The plasma spraying method according to claim 1 , wherein the metal thermal spray material is aluminum or an aluminum alloy.
7. The plasma spraying method according to claim 6 , further comprising performing a sealing treatment on the spray coating after said performing plasma spraying.
8. The plasma spraying method according to claim 6 , wherein the metal thermal spray material is an aluminum alloy comprising an aluminum-magnesium alloy or a zinc-aluminum alloy.
9. The plasma spraying method according to claim 1 , further comprising performing a sealing treatment on the spray coating after said performing plasma spraying.
10. The plasma spraying method according to claim 1 , wherein said roughening the surface of the metal body comprises using a grinding tool to form linear marks on the surface of the metal body, the linear marks crossing at an angle of intersection in a range of 60 degrees to 90 degrees.