Method of retarding quicklime for glass manufacture
A method is shown for retarding the reactivity of quicklime. The quicklime is contacted with an aqueous solution of a boron-containing compound after being calcined. The boron-containing solution can be sprayed on the quicklime as it moves past on a conveyor belt. The retarded quicklime can be used for various industrial purposes and is especially useful as a reactant in a glass making operation.
1. A method of retarding the reactivity of quicklime, comprising the steps of:
calcining a supply of limestone in a calcination step to form a source of quicklime;
after the calcination step, contacting the quicklime with a boron-containing compound to thereby form a chemically modified quicklime, the contact between the boron-containing compound and the quicklime being effective to retard the initial 30 second heat rise of the chemically modified quicklime to about 20-25° C. or below during subsequent slaking as measured according to ASTM C110; and
wherein the quicklime is contacted with 0.1 to 5% by weight, based upon the total weight of quicklime, of a 2-10% by volume solution of borax in water.
2. The method of claim 1 , wherein the quicklime is contacted with the solution of borax in water after it has been calcined but prior to grinding and further processing.
3. The method of claim 1 , wherein the boron-containing compound is provided as an aqueous solution which is added directly to a grinding mill as the quicklime is being ground.
4. The method of claim 1 , wherein the boron-containing compound is provided as an aqueous solution of borax which is sprayed onto the quicklime as it moves from a calciner to a grinding mill.
5. A method of retarding the reactivity of quicklime, comprising the steps of:
forming a saturated solution of borax in water;
using the saturated solution as a pretreatment which is applied to the quicklime after it has been calcined but prior to grinding and further processing, wherein the quicklime is treated with 0.1 to 5% by weight, based upon the total weight of quicklime, of a 2-10% by volume solution of borax in water; and
wherein the saturated solution of borax is applied to the quicklime by spraying the solution onto the quicklime as it moves on a conveyor from a calciner to a grinding mill.