Methods for in-situ generation of reactive etch and growth specie in film formation processes
Methods and apparatus are disclosed for the formation and utilization of metastable specie in a reaction chamber for processing substrates. The metastable specie may be used for etching the surface of substrates in situ, deposition processes during processing of the substrate.
1. A method of processing a wafer during a film-forming process in a reaction chamber comprising:
introducing a hydrogen-containing reactant gas into the reaction chamber;
introducing an etch chemical reactant that is spontaneously reactive with the hydrogen-containing gas in a separate conduit isolated from the hydrogen containing gas into the reaction chamber to provide reactant gas concentrations for the hydrogen containing gas and the etch chemical;
controlling one or more of the chamber partial pressure, temperature and the reactant gas concentrations below a value to prevent spontaneous reaction of the hydrogen containing gas and the etch chemical;
changing one or more of the chamber partial pressure, temperature and the reactant gas concentrations to react the hydrogen-containing gas and the etch chemical under controlled reaction conditions to form a metastable specie adjacent a surface of the wafer; and
utilizing the metastable specie in a subsequent growth or etch reaction.
2. The method of claim 1 , wherein the hydrogen-containing gas is in the form of a chemical precursor or a carrier gas.
3. The method of claim 2 , wherein the etch chemical is a halide-containing chemical.
4. The method of claim 3 , wherein the etch chemical is oxidizing.
5. The method of claim 3 , wherein the etch chemical is in molecular form.
6. The method of claim 3 , wherein the etch chemical is selected from the group consisting of HCl, HBr, Cl 2 , CH 3 Cl, CCI 4 , NF 3 , F 2 , CF 4 and combinations thereof.
7. The method of claim 1 , further comprising controlling the reaction by modulating the relative amounts of hydrogen and the etchant chemical introduced into the reaction chamber.
8. The method of claim 1 , further comprising controlling the reaction by adding a diluent gas to the reaction chamber.
9. The method of claim 8 , wherein the diluent gas includes an inert gas.
10. The method of claim 1 , wherein the process is a blanket film deposition processes.
11. The method of claim 1 , wherein the process is a selective film deposition processes.
12. The method of claim 1 , wherein reaction is utilized to improve incorporation of substituted chemical elements into the film.
13. The method of claim 12 , wherein the substituted chemical elements include carbon or dopants.
14. The method of claim 1 , wherein the method is used to improve the morphology of the film.
15. A method of processing a wafer during a film-forming process in a reaction chamber comprising;
delivering spontaneously reactive chemicals in separate conduits adjacent the wafer surface to provide reactant concentrations;
controlling one or more of the chamber partial pressure, temperature and the reactant concentrations below a value to prevent spontaneous reaction of the spontaneously reactive chemicals;
changing one or more of the chamber partial pressure, temperature and the reactant concentrations to react the chemicals under controlled conditions to form a metastable specie adjacent the wafer surface; and
utilizing the metastable species in a subsequent reaction.
16. The method of claim 15 , further comprising utilizing the metastable specie in an etching process.
17. The method of claim 15 , further comprising utilizing the metastable specie in a film growth process.
18. The method of claim 15 , wherein the chemicals are selected from the group consisting of H 2 , N 2 , SiH 4 , Si 2 H 6 , Si 3 H 8 , SiH 2 Cl 2 , Si 2 Cl 6 , Si 5 H 12 , GeH 4 , GeCl 4 , SiCH 6 , SiC 3 H 10 , HCl, HBr, Cl 2 , CH 3 Cl, CCI 4 , NF 3 , F 2 , CF 4 , and combinations thereof.
19. A method of processing a film on a wafer during a film-forming process in a reaction chamber comprising:
maintaining the temperature of the wafer below about 700° C.;
isolating Cl 2 and silane reactants from each other in separate conduits until the reactants are introduced into the reaction chamber;
controlling one or more of the chamber partial pressure, temperature and the reactant concentrations below a value to prevent spontaneous reaction of the Cl 2 and silane reactants;
changing one or more of the chamber partial pressure, temperature and the reactant concentration to react the Cl 2 and silane adjacent the wafer surface under controlled conditions to form a metastable SiCl x intermediate adjacent the wafer surface; and
depositing a film on the wafer surface utilizing the metastable SiCl x intermediate.
20. The method of claim 19 , further comprising isolating excess Cl 2 and etching a portion of the wafer.