Synthesis of lithium zirconate
A process is disclosed for the preparation of lithium zirconate and doped lithium zirconates for use as regenerable carbon dioxide sorbants by wet mixing zirconium hydroxide with lithium carbonate and then calcining the mixture. Due to the improved physical properties resulting from the disclosed preparation process, the lithium zirconates produced by this process are capable of absorbing carbon dioxide at high rates and in large amounts.
1. A process for the production of lithium zirconate comprising the steps of:
wet mixing zirconium hydroxide with lithium carbonate, and
calcining the mixture to form undoped said lithium zirconate having a formula, Li 2 ZrO 3 , or doped said lithium zirconate having a formula, Li n M′ 2-n Zr 1-2n O 3 , where n is at least 0.01 and M′ is one or more of Al, Na, Si, K, Mg and Y, and said doped and undoped lithium zirconate is in at least one of a tetragonal or monoclinic phase.
2. A process as claimed in claim 1 wherein the wet mixing is effected in an aqueous medium.
3. A process as claimed in claim 1 wherein the zirconium hydroxide is doped with a hydroxide of one or more of potassium, magnesium, sodium, lithium, yttrium, aluminum and silicon before being mixed with said lithium carbonate.
4. A process as claimed in claim 1 wherein one or more of potassium, magnesium, sodium, lithium, yttrium, aluminum and silicon salts are added during the mixing of zirconium hydroxide and lithium carbonate, the salts being capable of undergoing pyrolysis to form their corresponding oxides.
5. A process as claimed in claim 4 wherein the salts are carbonate salts.
6. A process as claimed in claim 1 wherein the calcination temperature is at least 700° C. but less than 800° C.
7. A process as claimed in claim 6 wherein the calcination temperature is at least 775° C., but less than 800° C.
8. A process as claimed in claim 1 wherein conditions of said calcining produce said doped or undoped lithium zirconate having a total pore volume of at least 0.002 cm 3 /g.
9. A process as claimed in claim 8 wherein said conditions of said calcining produce said doped or undoped lithium zirconate capable of absorbing 4.85 mol/kg of carbon dioxide.
10. A process as claimed in claim 8 wherein said conditions of said calcining produce said doped or undoped lithium zirconate having a surface area of at least 0.49 m 2 /g.
11. A process as claimed in claim 8 wherein said conditions of said calcining produce said doped or undoped lithium zirconate having a mean pore diameter of less than 75 nm.
12. A process as claimed in claim 1 comprising drying the mixture prior to said calcining.