Method of producing a powder, powder, and multilayered ceramic capacitor using the same
A core/shell structured powder different in composition between the inside the particle and the surface thereof before sintering, so that it is possible to sinter the powder at lower temperature and give a core/shell structured powder having a shell portion uniform in thickness after sintering; a multilayered ceramic capacitor having a longer lifetime, by preparing the multilayered ceramic capacitor by using a powder having a core/shell structure different in composition between the inside the particle and the surface thereof before sintering; and a method of producing a powder by synthesizing particles in the liquid containing a raw material, wherein particles different in composition at least between the inside the particle and the surface thereof are obtained by adding a composition to be incorporated as a component of the particles to the liquid during the synthetic process so that the composition of the liquid changes continuously or intermittently.
1. A method of producing a powder comprising synthesizing particles in a liquid comprising raw materials of two or more elements,
wherein particles different in composition at least between the inside the particle and the surface thereof are obtained by supplying a composition (1) to be incorporated as a component of the particles to the liquid so that the composition of the liquid changes continuously or intermittently during the synthetic process, wherein
the obtained particles are oxides having a perovskite structure,
the oxide having a perovskite structure is an oxide represented by ABO 3 , A represents at least one element selected from the group A consisting of barium, strontium, lead, rare-earth metals, magnesium, potassium, and sodium, and B represents at least one element selected from the group B consisting of titanium, zirconium, and niobium,
at least a raw material comprising group-A element A 1 and a raw material comprising group-B element B 1 are incorporated in the liquid in advance before initiation of synthesis,
the composition (1) comprises a raw material comprising another group-A element A 2 different from the A 1 element, and
the raw material comprising element A 1 and the raw material comprising element B 1 are reacted and thereafter the composition (1) is supplied to the liquid and reacted in the synthesis process, and
the particles having a composition of A 1 B 1 O 3 comprising the A 1 and B 1 elements as the principal components inside the particle and a composition of A 2 B 1 O 3 comprising the A 2 and B 1 elements as the principal components in the surface of the particle are obtained.
2. The method of producing a powder according to claim 1 ,
wherein the particles are synthesized by hydrothermal reaction.
3. The method of producing a powder according to claim 2 ,
wherein the particles are synthesized in an alkaline solution at 80° C. or higher.
4. The method of producing a powder according to claim 1 , wherein composition (1) is supplied continuously.
5. The method of producing a powder according to claim 1 , wherein composition (1) is supplied intermittently.
6. The method of producing a powder according to claim 1 , wherein composition (1) is supplied continuously and intermittently in combination.
7. The method of producing a powder according to claim 1 , wherein A 1 is barium, B 1 is titanium, and A 2 is strontium.