Non-fibrous polymer solution of para-aramid with high relative viscosity

1. A para-aramid pulp-like fiber derived from an anisotropic non-fibrous polymer solution, the solution comprising:

1-6wt. % para-aramid, which has to a maximum of 50 mole % of substituted aromatic diamines and to a maximum of 50 mole % of substituted aromatic dicarboxylic acid halide,

a polar amide solvent selected from the group consisting of N-methyl-2-pyrrolidone, N,N′ dimethylformamide, N,N′-dimethylacetamide, tetramethylurea, ad mixtures thereof;

an alkali or an alkaline earth metal chloride, in an amount of from 0.7 mole per mole of amide groups of the para-aramid, to 7.5 wt. % of the solution; and

water;

wherein:

at least 50 wt. % of formed hydrochloric acid is neutralized,

the solution does not comprise hex amethylphophoramide (HMPA),

the para-aramid pulp-like fiber is directly obtained without forming a yarn by spinning the solution through a nozzle into a low pressure zone whereby the solution is broken into droplets by contacting the solution with an air jet, followed by orienting the droplets by contacting the solution with an air jet, followed by orienting the droplets and coagulating the droplets in the low pressure zone by means of applying a coagulant jet.

2. The para-aramid pulp-like fiber of claim 1 , wherein the solution includes the para-aramid in either a mixture of N-methyl-2-pyrrolidone (NMP) and calcium chloride (CaCl2), or a mixture of dimethylacetamide (DMAc) and lithium chloride (LiCl).

3. The para-aramid pulp-like fiber of claim 1 , wherein the solution having a dynamic viscosity η dyn <10 Pa·s at a shear rate of 1000 s −1 .

4. A process for making the para-aramid pulp-like fiber of claim 1 comprising:

making an anisotropic solution comprising:

aromatic diamine and aromatic dicarboxylic acid halide monomers, and

a polar amide solvent selected from the group consisting of N-methyl-2-pyrrolidone, N,N′-dimethylformamide, N,N′-dimethylacetamide, tetramethylurea, and mixtures thereof,

polymerizing the monomers to form a 1 to 6 wt. % para-aramid in the polar amide solvent under a formation of hydrochloric acid, wherein the para-aramid has a maximum of 50 mole % of substituted aromatic diamines and to a maximum of 50 mole % of substituted aromatic dicarboxylic acid halide,

adding 0.5 to 4.5 wt. % of an alkali or an alkaline earth metal chloride during polymerization, in an amount corresponding to from at least 0.7 mole per mole of amide groups of the para-aramid to 7.5 wt. % of a final polymer solution,

neutralizing at least 50 wt. % of the formed hydrochloric acid with an inorganic or a strong organic base during or after the polymerization of the monomers to para-aramid to obtain the final polymer solution, and

spinning the final polymer solution to form the aramid pulp, wherein the aramid pulp is formed directly by the spinning without forming a yarn through a nozzle into a low pressure zone whereby the solution is broken into droplets by contacting the solution with an air jet, followed by orienting the droplets by contacting the solution with an air jet, followed by orienting the droplets and coagulating the droplets in the low pressure zone by means of applying a coagulant jet,

wherein the solution does not comprise HMPA.

5. The process according to claim 4 , wherein the formed hydrochloric acid is neutralized with calcium oxide, calcium hydroxide, lithium oxide or lithium hydroxide.

6. The process according to claim 4 , wherein the spinning is conducted at a temperature below 60° C.

7. The para-aramid pulp-like fiber of claim 1 , the para-aramid pulp-like fiber having a structural irregularity expressed as a difference in Canadian Standard Freeness (CSF) of never dried pulp and dried pulp of at least 100.

8. The para-aramid pulp-like fiber of claim 7 , wherein the difference in CSF of never dried pulp and dried pulp is at least 150.

9. The para-aramid pulp-like fiber of claim 7 , wherein the structural irregularity is contained in a kinky structure of a fibrous backbone of the pulp-like fiber.

10. The para-aramid pulp-like fiber of claim 7 , wherein a relative viscosity (η rel ) of the para-aramid pulp-like fiber is larger than 3.7.

11. A para-aramid paper formed from the para-aramid pulp-like fiber of claim 1 .

12. A para-aramid pulp-like fiber derived from an anisotropic non-fibrous polymer solution, the solution comprising:

1-6 wt. % poly(paraphenylene terephthalamide) (PPTA),

a polar amide solvent selected from the group consisting of N-methyl-2-pyrrolidone, N,N′ dimethylformamide, N,N′-dimethylacetamide, tetramethylurea, ad mixtures thereof;

an alkali or an alkaline earth metal chloride, in an amount of from 0.7 mole per mole of amide groups of the para-aramid, to 7.5 wt. % of the solution; and

water;

wherein:

at least 50 wt. % of formed hydrochloric acid is neutralized,

the solution does not comprise hex amethylphophoramide (HMPA),

the para-aramid pulp-like fiber is directly obtained without forming a yarn by spinning the solution through a nozzle into a low pressure zone whereby the solution is broken into droplets by contacting the solution with an air jet, followed by orienting the droplets by contacting the solution with an air jet, followed by orienting the droplets and coagulating the droplets in the low pressure zone by means of applying a coagulant jet.

13. The para-aramid pulp-like fiber of claim 1 , wherein the solution is comprise of 1.5 to 6 wt. % poly(paraphenyleneterephthalamide) (PPTA).

14. The process according to claim 4 , wherein the solution is comprised of 1.5 to 6 wt. % PPTA.

15. The process according to claim 14 , wherein the solution is an anisotropic solution comprised of 1.5 to 6 wt. % poly(paraphenylene terphthalamide) (PPTA).