Method for preparing titanium dioxide particles co-doped with nitrogen and fluorine
A method for preparing titanium dioxide particles co-doped with nitrogen and fluorine includes the steps of: mixing boric acid with ammonium fluorotitanate in an aqueous medium to form ammonium oxotrifluorotitanate; liquid-phase depositing the ammonium oxotrifluorotitanate on a silicon-containing substrate; and thermo-treating the ammonium oxotrifluorotitanate on the silicon-containing substrate at a temperature ranging from 300 to 1000° C.
1. A method for preparing titanium dioxide particles co-doped with nitrogen and fluorine, comprising the steps of:
mixing boric acid with ammonium fluorotitanate in an aqueous medium to form ammonium oxotrifluorotitanate;
liquid-phase depositing the ammonium oxotrifluorotitanate on a silicon-containing substrate; and
thermo-treating the ammonium oxotrifluorotitanate on the silicon-containing substrate at a temperature ranging from 400 to 800° C. to obtain the titanium dioxide particles co-doped with nitrogen and fluorine.
2. The method as claimed in claim 1 , wherein a molar ratio of the boric acid to the ammonium fluorotitanate ranges from 0.2 to 1.5.
3. The method as claimed in claim 2 , wherein the molar ratio is 0.6.
4. The method as claimed in claim 1 , wherein the boric acid and the ammonium fluorotitanate are mixed at 40° C.
5. The method as claimed in claim 1 , wherein the mixing step is conducted for 2 hours.
6. The method as claimed in claim 1 , wherein the silicon-containing substrate is made of a material selected from the group consisting of polysilicon, silicon nitride, glass, and quartz.
7. The method as claimed in claim 6 , wherein the silicon-containing substrate is made of glass.
8. The method as claimed in claim 1 , wherein the ammonium oxotrifluorotitanate is thermo-treated at 600° C.
9. The method as claimed in claim 1 , wherein the thermo-treating step is conducted under an atmosphere selected from the group consisting of oxygen, nitrogen, ozone, nitrous oxide, and inert gas.
10. A method for preparing titanium dioxide particles co-doped with nitrogen and fluorine, comprising the steps of:
mixing boric acid with ammonium fluorotitanate in an aqueous medium to form ammonium oxotrifluorotitanate;
liquid-phase depositing the ammonium oxotrifluorotitanate on a silicon-containing substrate; and
thermo-treating the ammonium oxotrifluorotitanate on the silicon-containing substrate at a temperature ranging from 300 to 1000° C.,
wherein the thermo-treating step is conducted under oxygen.
11. The method as claimed in claim 1 , wherein the thermo-treating step is conducted for a period ranging from 0.5 to 2 hours.
12. The method as claimed in claim 11 , wherein the thermo-treating step is conducted for 1 hour.