Method to manufacture composite polymer electrolyte membranes coated with inorganic thin films for fuel cells
The present invention, by coating the polymer electrolyte membranes for fuel cells with inorganic thin films via a PECVD method or a reactive sputtering method, reduces the methanol crossover sizably without seriously reducing the ionic conductivity of polymer electrolyte membranes, thereby, when applied to fuel cells, realizes a high performance of fuel cells. A surface of membrane can be coated with inorganic thin films made of inorganic materials, which are for example silicone oxide, titanium oxide, etc., so as to make composite polymer electrolyte membrane. For coating, plasma enhanced chemical vapor deposition method or reactive method can be used.
1. A method for manufacturing composite membranes for a fuel cell, comprising a step of coating a surface of polymer electrolyte membrane with inorganic thin film using a plasma enhanced chemical vapor deposition (PECVD) method, thereby obtaining the composite membrane,
wherein inorganic material of the inorganic thin film is one or more selected from the group consisting of silicon oxide (SiO 2 ), titanium oxide (TiO 2 ), zirconium oxide (ZrO 2 ), zirconium phosphate (Zr(HPO 4 ) 2 ), silicalite, and aluminum oxide (Al 2 O 3 );
the inorganic thin film is made by using one or more organic metal compound(s) selected from the group consisting of trimethyl disiloxanes (TMDSO), hexamethyl disilane, tetramethyl orthosilicate, tetrabutyl orthosilicate, tetra-isopropyl orthosilicate, aluminium methoxide, aluminium ethoxide, aluminium butoxide, aluminium isopropoxide, titanium ethoxide, titanium methoxide, titanium butoxide, titanium isopropoxide, zirconium ethoxide, and zirconium butoxide in conjunction with one or more gases selected from the group consisting of nitrogen, hydrogen, steam, and argon;
the inorganic thin film has a thickness of 1.0 nanometer (nm) to 500 nm;
the composite membranes have an ionic conductivity of 0.071 S/cm or more and
the composite membranes have a characteristic factor of 54 Ω −1 cm −3 s or more, wherein the characteristic factor equals (ionic conductivity/methanol permability)×10 −3 .
2. The method of claim 1 , wherein the polymer electrolyte membrane comprises perfluorosulfonic acid membrane; electrolyte membrane made of proton conducting hydrocarbon material; or electrolyte membrane made of proton conducting fluorine material.
3. The method of claim 1 wherein the PECVD method has a microwave power at the range of 10 watts to 500 watts.
4. The method of claim 1 wherein a reaction chamber pressure of the PECVD method is in the range of 1.0 to 1000 millitorr.
5. The method of claim 1 wherein an argon pre-treatment electromagnetic wave power of the PECVD method is in the range of 10 watts to 500 watts.
6. The method of claim 1 wherein a argon pre-treatment pressure of the PECVD method is in the range of 1.0 to 500 millitorr.
7. The method of claim 1 wherein a reaction gas pressure in a chamber of the PECVD method is in the range of 10 to 500 millitorr.
8. The method of claim 1 further comprising a step of coating a surface of the composite membrane with a proton-conducting ionomer solution, after coating the inorganic thin film on the surface of polymer electrolyte membrane, so as to enhance contact with electrodes during manufacturing membrane-electrode assembly.
9. A method for manufacturing an MEA comprising a step of coating catalyst for electrode directly on the composite manufactured according to claim 1 .