Porous sintered body, method of manufacturing porous sintered body, and method of manufacturing exhaust gas purifying apparatus
A method of manufacturing a porous sintered body includes mixing first silicon carbide particles, second silicon carbide particles, and a pore forming material having an average particle diameter Y μm to obtain a molding material. The first silicon carbide particles have an average particle diameter X μm larger than an average particle diameter of the second silicon carbide particles. Relationships 15≦X, 0.5·X≦Z≦0.9·X, and 0.8·Z≦Y≦1.8·Z are satisfied, wherein Z μm is an average pore diameter of the porous sintered body no less than 10 μm and no greater than 20 μm. The molding material is molded into a molded body. The molded body is degreased to eliminate the pore forming material from the molded body.
1. A method of manufacturing a porous sintered body, the method comprising:
mixing first silicon carbide particles, second silicon carbide particles, and a pore forming material having an average particle diameter Y pm to obtain a molding material, the first silicon carbide particles having an average particle diameter X μm larger than an average particle diameter of the second silicon carbide particles, relationships
15≦X ,
0.5 ·X≦Z≦ 0.9· X, and
0.8 ·Z≦Y≦ 1.8· Z
being satisfied, wherein Z μm is an average pore diameter of the porous sintered body no less than 10 μm and no greater than 20 μm;
molding the molding material into a molded body; and
degreasing the molded body to eliminate the pore forming material from the molded body.
2. The method of manufacturing a porous sintered body according to claim 1 , further comprising:
sintering the degreased molded body to form a porous sintered body.
3. The method of manufacturing a porous sintered body according to claim 2 , further comprising:
providing a catalyst on the porous sintered body.
4. The method of manufacturing a porous sintered body according to claim 3 , further comprising:
providing a catalyst carrying layer on the porous sintered body before providing the catalyst.
5. The method of manufacturing a porous sintered body according to claim 4 , wherein an oxide ceramic material is used as the catalyst carrying layer.
6. The method of manufacturing a porous sintered body according to claim 5 , wherein at least one of alumina, titania, zirconia, silica, and ceria is used as the catalyst carrying layer.
7. The method of manufacturing a porous sintered body according to claim 1 , wherein the molding material is molded into a molded body having a honeycomb structure.
8. The method of manufacturing a porous sintered body according to claim 7 , wherein the honeycomb structure has a plurality of cells partitioned by cell walls extending in a longitudinal direction of the honeycomb structure.
9. The method of manufacturing a porous sintered body according to claim 1 , wherein the porous sintered body is provided with porosity of 45% to 60%.
10. The method of manufacturing a porous sintered body according to claim 1 , wherein a synthetic resin is used as the pore forming material.
11. The method of manufacturing a porous sintered body according to claim 10 , wherein an acrylic material is used as the synthetic resin.
12. The method of manufacturing a porous sintered body according to claim 1 , wherein an organic polymer material is used as the pore forming material.
13. The method of manufacturing a porous sintered body according to claim 12 , wherein a starch material is used as the organic polymer material.
14. The method of manufacturing a porous sintered body according to claim 1 , wherein the first silicon carbide particles have the average particle diameter X of 15 μm to 40μm, and the second silicon carbide particles have the average particle diameter of 0.5 μm to 1.0 μm.
15. A porous sintered body comprising:
a body made by molding a molding material which comprises:
a pore forming material having an average particle diameter Y μm;
first silicon carbide particles having an average particle diameter X;
second silicon carbide particles having an average particle diameter smaller than the average particle diameter X; and
relationships
15≦X,
0.5· X≦Z≦ 0.9· X, and
0.8· Z≦Y≦ 1.8· Z
being satisfied, wherein Z pm is an average pore diameter of the porous sintered body no less than 10 μm and no greater than 20 μm.
16. A method of manufacturing an exhaust gas purifying apparatus, the method comprising:
mixing first silicon carbide particles, second silicon carbide particles, and a pore forming material having an average particle diameter Y μm to obtain a molding material, the first silicon carbide particles having an average particle diameter X μm larger than an average particle diameter of the second silicon carbide particles, relationships
15≦X,
0.5· X≦Z≦ 0.9· X, and
0.8· Z≦Y≦ 1.8· Z
being satisfied, wherein Z μm is an average pore diameter of the porous sintered body no less than 10 μm and no greater than 20 μm;
molding the molding material into a molded body;
degreasing the molded body to eliminate the pore forming material from the molded body;
sintering the degreased molded body to form a porous sintered body; and
providing the porous sintered body in a casing of the exhaust gas purifying apparatus.