Flash memory device and method of manufacturing the same
A flash memory device having a spacer of a gate region formed in an oxide-nitride-oxide (ONO) structure and a source/drain region formed using the ONO structure. The outermost oxide in the ONO structure is removed and an interlayer insulating film is formed to ensure sufficient space between the gate regions. Thus, it is possible to prevent a void from being generated in the interlayer insulating film and prevent a word line from being electrically connected to a drain contact for forming a bit line.
1. A method comprising:
forming a gate region including a tunnel oxide film, a floating gate, a dielectric film and a control gate over a semiconductor substrate;
forming a spacer film having a first oxide film, a nitride film, and a second oxide film against a sidewall of the gate region;
forming a spacer pattern by performing an entire surface etching on the spacer film;
forming a source/drain region by performing an ion implantation process using the spacer pattern and the gate region as a mask;
removing the second oxide film disposed at an outermost position of the spacer pattern after forming the source/drain region; and then
forming an interlayer insulating film over the semiconductor substrate with the gate region and a spacer formed thereon.
2. The method of claim 1 , wherein the second oxide film disposed at the outermost position of the spacer pattern is removed using a wet etching method.
3. The method of claim 2 , wherein a BHF solution is used as an etching solution in the wet etching method.
4. The method of claim 1 , wherein the first oxide film comprises TEOS.
5. The method of claim 4 , wherein the second oxide film comprises TEOS.
6. The method of claim 5 , wherein the nitride film comprises SiN.
7. The method of claim 6 , wherein the first oxide film has a thickness between approximately 150 to 300 Å.
8. The method of claim 7 , wherein the nitride film has a thickness between approximately 100 to 300 Å.
9. The method of claim 8 , wherein the second oxide film has a thickness between approximately 500 to 800 Å.