Silica-coated alumina activator-supports for metallocene catalyst compositions
Silica-coated alumina activator-supports, and catalyst compositions containing these activator-supports, are disclosed. Methods also are provided for preparing silica-coated alumina activator-supports, for preparing catalyst compositions, and for using the catalyst compositions to polymerize olefins.
1. An olefin polymerization process, the process comprising:
contacting a catalyst composition with at least one olefin monomer and optionally at least one olefin comonomer under polymerization conditions to produce an olefin polymer, wherein the catalyst composition comprises at least one transition metal compound comprising titanium, zirconium, or hafnium, and at least one activator-support, wherein:
the at least one activator-support comprises at least one silica-coated alumina treated with at least one electron-withdrawing anion, wherein:
the at least one silica-coated alumina has a weight ratio of alumina to silica in a range from about 1:1 to about 100:1, and
the at least one electron-withdrawing anion comprises fluoride, chloride, bromide, phosphate, triflate, bisulfate, sulfate, or any combination thereof.
2. The process of claim 1 , wherein the at least one olefin monomer is ethylene, and the at least one olefin comonomer comprises propylene, 1-butene, 2-butene, 3-methyl-1-butene, isobutylene, 1-pentene, 2-pentene, 3-methyl-1-pentene, 4-methyl-1-pentene, 1-hexene, 2-hexene, 3-ethyl-1-hexene, 1-heptene, 2-heptene, 3-heptene, 1-octene, 1-decene, styrene, or a combination thereof.
3. The process of claim 1 , wherein the olefin polymer has less than about 5 long chain branches (LCB) per million total carbon atoms.
4. The process of claim 1 , wherein the olefin polymer has a CY-a parameter in a range from about 0.4 to about 0.7.
5. An olefin polymerization process, the process comprising:
contacting a catalyst composition with at least one olefin monomer and optionally at least one olefin comonomer under polymerization conditions to produce an olefin polymer, wherein the catalyst composition comprises at least one metallocene compound and at least one activator-support, wherein:
the at least one activator-support comprises at least one silica-coated alumina treated with at least one electron-withdrawing anion, wherein:
the at least one silica-coated alumina has a weight ratio of alumina to silica in a range from about 1:1 to about 100:1, and
the at least one electron-withdrawing anion comprises fluoride, chloride, bromide, phosphate, triflate, bisulfate, sulfate, or any combination thereof.
6. The process of claim 5 , wherein the weight ratio of alumina to silica is in a range from about 2:1 to about 20:1.
7. The process of claim 5 , wherein the weight ratio of alumina to silica is in a range from about 2:1 to about 12:1.
8. The process of claim 5 , wherein the at least one activator-support comprises at least one silica-coated alumina treated with at least two electron-withdrawing anions, and wherein the at least two electron-withdrawing anions comprise fluoride and phosphate, fluoride and sulfate, chloride and phosphate, chloride and sulfate, triflate and sulfate, or triflate and phosphate.
9. The process of claim 5 , wherein the at least one silica-coated alumina has a surface area in a range from about 100 to about 1000 m 2 /g, a pore volume greater than about 0.5 mL/g, and a particle size in a range from about 5 microns to about 150 microns.
10. The process of claim 5 , wherein the at least one silica-coated alumina is produced by a process comprising:
providing at least one alumina source, the at least one alumina source comprising an alumina, a hydrated alumina, aluminum hydroxide, boehmite, or a combination thereof;
contacting the at least one alumina source with a solution or suspension comprising at least one solvent and at least one silicon-containing compound capable of producing silica upon calcination;
depositing a coating of the at least one silicon-containing compound on at least a portion of the at least one alumina source; and
removing the solvent.
11. The process of claim 5 , wherein the catalyst composition further comprises at least one organoaluminum compound having the formula:
Al(X 9 ) m (X 10 ) 3-m ;
wherein:
X 9 is a hydrocarbyl;
X 10 is an alkoxide or an aryloxide, a halide, or a hydride; and
m is from 1 to 3, inclusive.
12. The process of claim 5 , wherein the catalyst composition further comprises at least one optional co-catalyst, wherein the at least one optional co-catalyst is at least one aluminoxane compound, at least one organoboron or organoborate compound, at least one ionizing ionic compound, or any combination thereof.
13. The process of claim 5 , wherein the at least one olefin monomer is ethylene or propylene.
14. The process of claim 5 , wherein the at least one olefin monomer is ethylene, and the at least one olefin comonomer comprises propylene, 1-butene, 2-butene, 3-methyl-1-butene, isobutylene, 1-pentene, 2-pentene, 3-methyl-1-pentene, 4-methyl-1-pentene, 1-hexene, 2-hexene, 3-ethyl-1-hexene, 1-heptene, 2-heptene, 3-heptene, 1-octene, 1-decene, styrene, or a combination thereof.
15. The process of claim 5 , wherein the polymerization process is conducted in a batch reactor, a slurry reactor, a gas phase reactor, a solution reactor, a high pressure reactor, a tubular reactor, an autoclave reactor, or a combination thereof.
16. The process of claim 5 , wherein the at least one metallocene compound comprises an ansa-metallocene compound.
17. The process of claim 5 , wherein the at least one metallocene compound comprises an unbridged metallocene compound.
18. An olefin polymerization process, the process comprising:
contacting a catalyst composition with at least one olefin monomer and optionally at least one olefin comonomer under polymerization conditions to produce an olefin polymer, wherein the catalyst composition comprises:
(a) at least one metallocene compound;
(b) at least one activator-support; and
(c) at least one organoaluminum compound;
wherein the at least one organoaluminum compound comprises trimethylaluminum, triethylaluminum, tri-n-propylaluminum, tri-n-butylaluminum, triisobutylaluminum, tri-n-hexylaluminum, tri-n-octylaluminum, diisobutylaluminum hydride, diethylaluminum ethoxide, diethylaluminum chloride, or any combination thereof;
wherein the at least one activator-support comprises at least one silica-coated alumina treated with at least one electron-withdrawing anion, wherein:
the at least one silica-coated alumina has a weight ratio of alumina to silica in a range from about 2:1 to about 20:1, and
the at least one electron-withdrawing anion comprises fluoride, chloride, bromide, phosphate, triflate, bisulfate, sulfate, or any combination thereof.
19. The process of claim 18 , wherein a catalyst activity of the catalyst composition is greater than about 1000 grams of polyethylene per gram of activator-support per hour under slurry polymerization conditions, using isobutane as a diluent, with a polymerization temperature of 90° C. and a reactor pressure of 420 psig.
20. The process of claim 18 , wherein a catalyst activity of the catalyst composition is greater than about 25,000 grams of polyethylene per gram of metallocene compound per hour under slurry polymerization conditions, using isobutane as a diluent, with a polymerization temperature of 90° C. and a reactor pressure of 420 psig.