Method of manufacturing grin lens and grin lens
The manufacture of a GRIN lens using a sol-gel process includes forming a wet gel from an alcohol solution containing a silicon alkoxide, a dopant alkoxide, and an aluminum alkoxide, first, an alcohol solution containing the silicon alkoxide and the aluminum alkoxide as is prepared, and then the dopant alkoxide is mixed thereto.
1. A method of manufacturing a GRIN lens comprising:
forming a wet gel from an alcohol solution containing a silicon alkoxide, a dopant alkoxide, and an aluminum alkoxide;
dissolving by leaching the dopant and aluminum away from an outer peripheral surface of the wet gel to provide a refractive index distribution;
forming a dry gel by drying the wet gel;
forming a glass preform by firing the dry gel; and
wire-drawing the preform,
wherein, during said forming the wet gel, the alcohol solution is prepared by first forming an alcohol solution containing the silicon alkoxide and the aluminum alkoxide, and then mixing the dopant alkoxide thereto.
2. The method of manufacturing a GRIN lens according to claim 1 , wherein the dopant is at least one selected from a group consisting of Ti, Ta, Sb, and Zr.
3. The method of manufacturing a GRIN lens according to claim 1 , wherein a concentration of elemental aluminum contained in the dry gel formed during said forming the dry gel is 0.04 mole percent or more based on (elemental silicon+elemental dopant+elemental aluminum).
4. The method of manufacturing a GRIN lens according to claim 3 , wherein the dopant is at least one selected from a group consisting of Ti, Ta, Sb, and Zr.
5. The method of manufacturing a GRIN lens according to claim 1 , wherein a concentration of elemental aluminum contained in the alcohol solution during said forming the wet gel is 2 to 20 mole percent based on (elemental silicon+elemental dopant+elemental aluminum).
6. The method of manufacturing a GRIN lens according to claim 5 , wherein the dopant is at least one selected from a group consisting of Ti, Ta, Sb, and Zr.