Polyvinyl alcohol fibers, and nonwoven fabric comprising them
Readily-fibrillable fibers of PVA polymer, having good chemical resistance, hydrophilicity, weather resistance and water resistance have a flattened cross-sectional profile and have a mean thickness D (μm) that satisfies the following formula (1): 0.4≦D≦5 (1) wherein D=S/L; S indicates the cross-section area (μm 2 ) of the fibers; and L indicates the length (μm) of the major side of the cross section of the fibers. The fibers can be used for making nonwoven fabrics.
1. Polyvinyl alcohol fibers having an extremely flattened cross-sectional profile and having a mean thickness D (μm) that satisfies the following formula (1):
0.4≦D≦5 (1),
wherein
D=S/L;
D indicates the mean thickness (μm) of the fibers which is a mean length (μm) of the minor side of the cross section of the fibers;
S indicates the cross-section area (μm 2 ) of the fibers; and
L indicates the length (μm) of the major side of the cross section of the fibers;
wherein said polyvinyl alcohol fibers consist of polyvinyl alcohol and from 0.01 to 30% by mass of a layered compound having a mean particle size of from 0.01 to 30 μm and wherein said layered compound is smectite, montmorillonite or mica.
2. Polyvinyl alcohol fibers as claimed in claim 1 , which satisfy the following formula (2):
10 ≦L/D≦ 50 (2)
wherein
D indicates the mean thickness (μm) of the fibers; and
L indicates the length (μm) of the major side of the cross section of the fibers.
3. Polyvinyl alcohol fibers as claimed in claim 1 , wherein one end or both ends of the extremely flattened cross-sectional profile of the fibers are branched.
4. Polyvinyl alcohol fibers as claimed in claim 1 , wherein said fibers have a water-absorbing speed of 123-128 mm/5 min.
5. Polyvinyl alcohol fibers as claimed in claim 1 , wherein when said fibers are used to wipe off a transparent acrylic plate spotted with Indian ink, a residue after wiping is 3.1 to 5.0%.
6. A dry-process nonwoven fabric, comprising:
the polyvinyl alcohol fibers as claimed in claim 1 ;
wherein said dry-process fabric is obtained by
applying a water jet of 30 kg/cm 2 or more to a web that comprises said fibers, or
needle-punching the web to a punching density of at least 250 kg/cm 2 to thereby fibrillate said fibers.
7. The non-woven fabric as claimed in claim 6 , wherein said fibers satisfy the following formula (2):
10 ≦L/D≦ 50 (2)
wherein
D indicates the mean thickness (μm) of the fibers; and
L indicates the length (μm) of the major side of the cross section of the fibers.
8. The non-woven fabric as claimed in claim 6 , wherein one end or both ends of the extremely flattened cross-sectional profile of the fibers are branched.
9. A wet-process water-jet nonwoven fabric, comprising:
the polyvinyl alcohol fibers as claimed in claim 1 ;
wherein said wet-process water-jet nonwoven fabric is obtained by applying a water jet of 30 kg/cm 2 or more to base paper prepared from a slurry that comprises said fibers as a part of the fibrous component thereof, to thereby fibrillate the fibers.
10. The non-woven fabric as claimed in claim 9 , wherein said fibers satisfy the following formula (2):
10 ≦L/D≦ 50 (2)
wherein
D indicates the mean thickness (μm) of the fibers; and
L indicates the length (μm) of the major side of the cross section of the fibers.
11. The non-woven fabric as claimed in claim 9 , wherein one end or both ends of the extremely flattened cross-sectional profile of the fibers are branched.
12. Polyvinyl alcohol fibers having an extremely thinly flattened cross-sectional profile and having a mean thickness D (μm) that satisfies the following formula (1):
0.4≦D≦5 (1),
wherein
D=S/L;
D indicates the mean thickness (μm) of the fibers which is a mean length (μm) of the minor side of the cross section of the fibers;
S indicates the cross-section area (μm 2 ) of the fibers; and
L indicates the length (μm) of the major side of the cross section of the fibers;
wherein said polyvinyl alcohol fibers consist of polyvinyl alcohol and from 0.01 to 30% by mass of a layered compound having a mean particle size of from 0.01 to 30 μm and wherein said layered compound is smectite, montmorillonite or mica.
13. Polyvinyl alcohol fibers as claimed in claim 12 , which satisfy the following formula (2):
10 ≦L/D≦ 50 (2)
wherein
D indicates the mean thickness (μm) of the fibers; and
L indicates the length (μm) of the major side of the cross section of the fibers.
14. Polyvinyl alcohol fibers as claimed in claim 12 , wherein one end or both ends of the extremely flattened cross-sectional profile of the fibers are branched.
15. Polyvinyl alcohol fibers as claimed in claim 12 , wherein one end or both ends of the extremely flattened cross-sectional profile of the fibers are branched.
16. Polyvinyl alcohol fibers as claimed in claim 12 , wherein said fibers have a water-absorbing speed of 123-128 mm/5 min.
17. Polyvinyl alcohol fibers as claimed in claim 12 , wherein when said fibers are used to wipe off a transparent acrylic plate spotted with Indian ink, a residue after wiping is 3.1 to 5.0%.
18. A method for producing a dry-process nonwoven fabric, said method comprising:
applying a water jet of 30 kg/cm 2 or more to a web that contains the fibers of claim 1 , or
needle-punching the web to a punching density of at least 250 kg/cm 2 to thereby fibrillate the fibers.
19. The method as claimed in claim 18 , wherein said fibers satisfy the following formula (2):
10 ≦L/D≦ 50 (2)
wherein
D indicates the mean thickness (μm) of the fibers; and
L indicates the length (μm) of the major side of the cross section of the fibers.
20. The method as claimed in claim 18 , wherein one end or both ends of the extremely flattened cross-sectional profile of the fibers are branched.
21. A dry-process nonwoven fabric obtained according to the method of claim 18 .
22. The nonwoven fabric as claimed in claim 21 , wherein said fibers satisfy the following formula (2):
10 ≦L/D≦ 50 (2)
wherein
D indicates the mean thickness (μm) of the fibers which is a mean length (μm) of the minor side of the cross section of the fibers; and
L indicates the length (μm) of the major side of the cross section of the fibers.
23. The nonwoven fabric as claimed in claim 21 , wherein one end or both ends of the extremely flattened cross-sectional profile of the fibers are branched.
24. A method for producing a wet-process water-jet nonwoven fabric, which comprises:
applying a water jet of 30 kg/cm 2 or more to base paper prepared from a slurry that contains the fibers of claim 1 as a part of the fibrous component thereof, to thereby fibrillate the fibers.
25. The method as claimed in claim 24 , wherein said fibers satisfy the following formula (2):
10 ≦L/D≦ 50 (2)
wherein
D indicates the mean thickness (μm) of the fibers; and
L indicates the length (μm) of the major side of the cross section of the fibers.
26. The method as claimed in claim 24 , wherein one end or both ends of the extremely flattened cross-sectional profile of the fibers are branched.
27. A wet-process nonwoven fabric obtained according to the method of claim 24 .
28. The nonwoven fabric as claimed in claim 27 , wherein said fibers satisfy the following formula (2):
10 ≦L/D≦ 50 (2)
wherein
D indicates the mean thickness (μm) of the fibers which is a mean length (μm) of the minor side of the cross section of the fibers; and
L indicates the length (μm) of the major side of the cross section of the fibers.
29. The nonwoven fabric as claimed in claim 27 , wherein one end or both ends of the extremely flattened cross-sectional profile of the fibers are branched.