Self-releasing curing bladder
This invention relates to an expandable curing bladder for use in curing rubber products; the bladder comprising an inner layer and an outer layer bonded to the first layer; the inner layer comprising a rubber composition comprised of, based on parts weight per 100 parts by weight rubber (phr): an isobutylene copolymer rubber selected from butyl rubber and/or halobutyl rubber, wherein said butyl rubber comprises a copolymer of isobutylene and isoprene which contains from about 0.5 to about 5 weight percent units derived from isoprene; wherein said halobutyl rubber is a halogenated butyl rubber comprises a chlorinated or brominated copolymer of isobutylene and isoprene which contains from about 0.5 to about 5 weight percent units derived from isoprene; and the outer layer comprising a rubber composition comprising a silicon rubber.
1. An expandable curing bladder for use in curing rubber products; the bladder comprising an inner layer and a calendered outer layer bonded to the inner layer, wherein the outer layer has a thickness ranging from about 0.025 to about 0.25 cm, and the inner layer is thicker than the outer layer;
the inner layer comprising a rubber composition comprised of, based on parts weight per 100 parts by weight rubber (phr): an isobutylene copolymer rubber selected from butyl rubber and/or halobutyl rubber,
wherein said butyl rubber comprises a copolymer of isobutylene and isoprene which contains from about 0.5 to about 5 weight percent units derived from isoprene;
wherein said halobutyl rubber is a halogenated butyl rubber comprising a chlorinated or brominated copolymer of isobutylene and isoprene which contains from about 0.5 to about 5 weight percent units derived from isoprene; and
the outer layer comprising a rubber composition comprising a silicone rubber; wherein said silicone rubber is formed from a composition comprising an organopolysiloxane containing at least 2 silicon-bonded alkenyl groups per molecule, an organohydrogenpolysiloxane having at least 2 silicon-bonded hydrogen atoms in each molecule, an inorganic filler, and a hydrosilylation catalyst.
2. The expandable curing bladder of claim 1 for use in curing pneumatic rubber tires.
3. The expandable curing bladder of claim 1 wherein said catalyst is a platinum-containing hydrosilylation catalyst.
4. A curing press for curing an uncured toroidally shaped pneumatic rubber tire which contains said expandable curing bladder of claim 1 to assist shaping and curing said pneumatic tire.
5. The expandable curing bladder of claim 1 , wherein the rubber composition of the outer layer further comprises and adhesion promoter.
6. The expandable curing bladder of claim 5 , wherein the adhesion promoter is selected from the group consisting of (i) a polysiloxane having an average of at least one silicon-bonded alkenyl group and an average of at least one silicon-bonded hydroxyl group per molecule, and (ii) an epoxy-containing polysiloxaneis.