Narrow band omnidirectional reflectors and their use as structural colors
View Patent ↗Disclosed is a multilayer structure wherein a first layer of a first material having an outer surface and a refracted index between 2 and 4 extends across an outer surface of a second layer having a refractive index between 1 and 3. The multilayer stack has a reflective band of less than 200 nanometers when viewed from angles between 0° and 80° and can be used to reflect a narrow range of electromagnetic radiation in the ultraviolet, visible and infrared spectrum ranges. In some instances, the reflection band of the multilayer structure is less than 100 nanometers. In addition, the multilayer structure can have a quantity defined as a range to mid-range ratio percentage of less than 2%.
1. An omnidirectional reflector comprising:
alternating first and second layers, said first layer of a first material having a first predefined thickness with an outer surface and a refractive index between 2 and 4; and
said second layer of a second material having a second predefined thickness with an outer surface and a refractive index between 1 and 3, said outer surface of said second layer extending across said outer surface of said first layer, said first layer in direct contact with and extending across said second layer;
wherein said first layer and said second layer have a refractive index contrast between 0.2 and 1.0;
said first predefined thickness, said second predefined thickness and said refractive index contrast between 0.2 and 1.0 providing a multilayer stack having a reflection band of less than 200 nanometers when viewed from angles between 0 degrees and 80 degrees;
said multilayer stack having more than three layers.
2. The omnidirectional reflector of claim 1 , wherein said reflection band is less than 200 nanometers when viewed from angles between 0 degrees and 65 degrees.
3. The omnidirectional reflector of claim 1 , wherein said reflection band is less than 100 nanometers when viewed from angles between 0 degrees and 65 degrees.
4. The omnidirectional reflector of claim 1 , wherein said refractive index contrast is between 0.2 and 0.6.
5. The omnidirectional reflector of claim 1 , wherein said multilayer stack has a range to mid-range ratio percentage between a value greater than zero and 10%.
6. The omnidirectional reflector of claim 1 , wherein said multilayer stack has a range to mid-range ratio percentage between a value greater than zero and 5%.
7. The omnidirectional reflector of claim 1 , wherein said multilayer stack has a range to mid-range ratio percentage between a value greater than zero and 2%.
8. The omnidirectional reflector of claim 1 , wherein said multilayer stack has more than seven total layers.
9. The omnidirectional reflector of claim 1 , wherein said multilayer stack is in the form of a flake.
10. The omnidirectional reflector of claim 9 , wherein said flake has an average thickness range of between 0.5 and 5 microns.
11. The omnidirectional reflector of claim 9 , wherein said flake has an average diameter range of between 5 and 50 microns.
12. The omnidirectional reflector of claim 9 , wherein said flake is mixed with a binder to make a paint.
13. The omnidirectional reflector of claim 9 , wherein said flake is mixed with a binder to make a UV-protective coating.
14. An omnidirectional reflector comprising:
alternating first and second layers, said first layer of a first material having a first predefined thickness with an outer surface and a refractive index between 2 and 4; and
said second layer of a second material having a second predefined thickness with an outer surface and a refractive index between 1 and 3, said outer surface of said second layer extending across said outer surface of said first layer, said first layer extending across said second layer;
wherein said first layer and said second layer have a refractive index contrast between 0.2 and 1.0;
said first predefined thickness, said second predefined thickness and said refractive index contrast between 0.2 and 1.0 providing a multilayer stack having a reflection band of less than 200 nanometers when viewed from angles between 0 degrees and 80 degrees;
said alternating first and second layers in the form of a flake having an average thickness range of between 0.5 and 5 microns.
15. The omnidirectional reflector of claim 14 , wherein said flake has an average diameter range of between 5 and 50 microns.
16. The omnidirectional reflector of claim 14 , wherein said flake is mixed with a binder to make a paint.
17. The omnidirectional reflector of claim 14 , wherein said flake is mixed with a binder to make a UV-protective coating.
18. The omnidirectional reflector of claim 14 , wherein said reflection band is less than 200 nanometers when viewed from angles between 0 degrees and 65 degrees.
19. The omnidirectional reflector of claim 14 , wherein said reflection band is less than 100 nanometers when viewed from angles between 0 degrees and 65 degrees.