Molded ferrite sheet, sintered ferrite substrate and antenna module
The present invention relates to a molded ferrite sheet having opposing surfaces and a thickness in a range of 30 μm to 430 μm, at least one surface of said opposing surfaces having the following surface roughness characteristics (a) to (c): (a) a center line average roughness is in a range of 170 nm to 800 nm, (b) a maximum height is in a range of 3 μm to 10 μm, and (c) an area occupancy rate of cross-sectional area taken along a horizontal plane at a depth of 50% of the maximum height in a square of side 100 μm is in a range of 10 to 80%.
1. A sintered ferrite substrate having opposing surfaces and a thickness in a range of 25 μm to 360 μm, at least one surface of said opposing surfaces having the following surface roughness characteristics (a) to (c):
(a) a center line average roughness is in a range of 150 nm to 700 nm,
(b) a maximum height is in a range of 2 μm to 9 μm, and
(c) an area occupancy rate of cross-sectional area taken along a horizontal plane at a depth of 50% of the maximum height in a square of side 100 μm is in a range of 10 to 80%.
2. A sintered ferrite substrate as recited in claim 1 , wherein a conductive layer is provided on one of the opposing surfaces of the sintered ferrite substrate.
3. A sintered ferrite substrate as recited in claim 1 , wherein grooves are formed on at least one of the opposing surfaces of the sintered ferrite substrate.
4. A sintered ferrite substrate as recited in claim 1 , wherein an adhesive film is adhered to at least one of the opposing surfaces of the sintered ferrite substrate and wherein the sintered ferrite substrate is divided into a plurality of parts.
5. A sintered ferrite substrate having opposing surfaces and a thickness in a range of 25 μm to 360 μm, at least one surface of said opposing surfaces having the following surface roughness characteristics (a) to (c):
(a) a center line average roughness is in a range of 150 nm to 700 nm,
(b) a maximum height is in a range of 2 μm to 9 μm, and
(c) an area occupancy rate of cross-sectional area taken along a horizontal plane at a depth of 50% of the maximum height in a square of side 100 μm is in a range of 10 to 80%,
wherein the ferrite is Ni—Zn—Cu-based spinel ferrite and wherein said sintered ferrite substrate has a magnetic permeability with a real part μr′ and an imaginary part μr″ of not less than 80 and not greater than 20, respectively, at 13.56 MHz.
6. A sintered ferrite substrate having opposing surfaces and a thickness in a range of 25 μm to 360 μm, at least one surface of said opposing surfaces having the following surface roughness characteristics (a) to (c):
(a) a center line average roughness is in a range of 150 nm to 700 nm,
(b) a maximum height is in a range of 2 μm to 9 μm, and
(c) an area occupancy rate of cross-sectional area taken along a horizontal plane at a depth of 50% of the maximum height in a square of side 100 μm is in a range of 10 to 80%,
wherein the ferrite is Mg—Zn—Cu-based spinel ferrite and wherein said sintered ferrite substrate has a magnetic permeability with a real part μr′ and an imaginary part μr″ of not less than 80 and not greater than 100, respectively, at 13.56 MHz.