Adsorbent, adsorption apparatus, and method for manufacturing the adsorption apparatus
View Patent ↗In an adsorbent of the present invention, at least a surface and its vicinity thereof is composed of an apatite represented by the formula Ca 10 (PO 4 ) 6 ((OH) 1-x A x ) 2 , where A represents a halogen element and 0≦x≦1, and a phosphate group contained in the apatite is bonded to a trivalent metal ion. Further, preferably, the trivalent metal ion is Fe 3+ . According to the present invention, it is possible to provide an adsorbent capable of specifically adsorbing an object compound, an adsorption apparatus capable of separating and purifying the object compound easily and reliably, and a method capable of manufacturing such an adsorption apparatus easily in a short time.
1. A method for manufacturing an adsorption apparatus, the adsorption apparatus comprising a column having an adsorbent filling space, and an adsorbent filled into the adsorbent filling space of the column, wherein the adsorbent comprises a plurality of apatite particles, each having a surface, and each comprising an apatite represented by the formula Ca 10 (PO 4 ) 6 ((OH) 1-x A x ) 2 , where A represents a halogen element and 0.3≦x≦1, and Fe 3 ′ bonded to a phosphate group contained in the apatite forming the surface of each of the apatite particles, and wherein average particle size of the apatite particles is in the range of 0.5 to 100 μm and the amount of the Fe 3+ to be bonded to the apatite forming the surface of each of the apatite particles is in the range of 0.1 to 100 mg per gram of the apatite,
the method comprising:
preparing the column in which the adsorbent filling space is filled with said apatite particles; and
passing a solution containing Fe 3+ through the adsorbent filling space of the column at a flow rate of 0.1 to 10 ml/min so that the Fe 3+ is selectively bonded to the phosphate group contained in the apatite forming the surface of each of the apatite particles so as to obtain said adsorbent.
2. The method for manufacturing an adsorption apparatus as claimed in claim 1 , wherein the amount of the Fe 3+ contained in 1 L of the solution is in the range of 1 to 50 mol per 1 mol of the apatite.
3. The method for manufacturing an adsorption apparatus as claimed in claim 1 , wherein the total amount of the solution containing the Fe 3+ to be passed through the adsorbent filling space is in the range of 1 to 50 mL.
4. The method for manufacturing an adsorption apparatus as claimed in claim 1 , wherein the solution comprises FeCl 3 .
5. The method for manufacturing an adsorption apparatus as claimed in claim 1 , wherein the A is a fluorine element.
6. The method for manufacturing an adsorption apparatus as claimed in claim 1 , wherein the adsorbent filling space is substantially fully filled with the adsorbent.
7. The method for manufacturing an adsorption apparatus as claimed in claim 1 , wherein all the adsorbent contained in the adsorbent filling space has substantially the same composition.
8. An adsorbent capable of adsorbing a phosphorylated protein, the adsorbent comprising a plurality of apatite particles each having a surface and each comprising an apatite represented by the formula Ca 10 (PO 4 ) 6 ((OH) 1-x A x ) 2 , where A represents a halogen element and 0.3≦x≦1, and Fe 3+ bonded to a phosphate group contained in the apatite forming the surface of each of the apatite particles, and wherein average particle size of the apatite particles is in the range of 0.5 to 100 μm and the amount of the Fe 3+ to be bonded to the apatite forming the surface of each of the apatite particles is in the range of 0.1 to 100 mg per gram of the apatite.
9. The adsorbent as claimed in claim 8 , wherein the A is a fluorine element.