Adjuvant for hydraulic compositions
The invention provides an admixture for a hydraulic binder composition comprising at least one cationic polymer and at least one anionic polymer, at least one of these polymers having a comb type of structure, wherein the mass ratio of the anionic polymer/cationic polymer is from 99.9/0.1 to 60/40. It also provides a process for its preparation as well as its use as a plasticizer.
1. A method of fluidizing a cement composition comprising cement and water, comprising:
forming a plasticizing admixture corresponding to a solution comprising at least one cationic polymer and at least one anionic polymer, at least one of the polymers having a comb type of structure, and the anionic polymer/cationic polymer mass ratio being from 99.9/0.1 to 60/40; and adding the solution to the cement composition in an amount of from 0.10% to 1% dry weight, related to the weight of the cement.
2. The method according to claim 1 , wherein the addition of the admixture modifies the fluidity retention of the cement composition.
3. The method according to claim 1 , wherein the anionic polymer comprises silanol side groups.
4. The method according to claim 1 , wherein the anionic polymer of the plasticizer admixture has a comb type of structure.
5. The method according to claim 4 , wherein the polymer having a comb type of structure comprises moieties on its main chain derived from methacrylic acid.
6. The method according to claim 1 , wherein the polymer having the comb type structure of the plasticizer admixture comprises polyoxyalkylenated side groups.
7. The method according to claim 1 , wherein the anionic polymer has an intrinsic viscosity lower than 1.5 dl/g.
8. The method according to one of claim 1 , wherein the anionic polymer has an intrinsic viscosity lower than 1.0 dl/g.
9. The method according to claim 1 , wherein the anionic polymer has an intrinsic viscosity lower than 0.8 dl/g.
10. The method according to claim 1 , wherein the cationic polymer's cationicity does not depend on the pH.
11. A composition formed according to the method of claim 1 .
12. The method according to claim 1 , wherein the admixture reduces the required amount of water added to the cement composition.