Anticorrosion agents for halide brines
Halide brine solutions that contain a dissolved salt of an alkali metal halide or alkali earth metal halide, and an anticorrosion agent comprising an alcohol diglycinate are described. The halide brine solutions may be used to treat transportation surfaces for deicing, anti-freezing, and dust suppression, among other applications. For example, methods of treating a transportation surface with a deicing composition to slow the formation of ice and snow on the surface are described. These methods may include providing the deicing composition that includes an aqueous solution of magnesium chloride, and an ethanoldiglycinate disodium salt. The deicing composition may be sprayed on the transportation surface in an amount effective to slow the formation of ice and snow on the surface.
1. An anti-icing solution comprising:
a dissolved salt comprising magnesium chloride; and
an anticorrosion agent comprising an alcohol diglycinate.
2. The anti-icing solution of claim 1 , wherein the alcohol diglycinate has the chemical formula:
where n=1-5, and X and Y are, independently, alkali metal cations.
3. The anti-icing solution of claim 2 , wherein n=2, and X and Y are sodium ions.
4. The anti-icing agent of claim 1 , wherein the anticorrosion agent reduces a corrosion rate by about 70% or more compared with an aqueous solution that only contains the dissolved salt.
5. The anti-icing agent of claim 1 , wherein the concentration of the dissolved salt of magnesium chloride is about 5% to about 30%, by wt.
6. The anti-icing agent of claim 1 , wherein the concentration of the anticorrosion agent in the solution is about 0.1%, by wt., or more.
7. The anti-icing agent of claim 1 , wherein the concentration of the anticorrosion agent in the solution is about 0.1% to about 0.5%, by wt.
8. A method of treating a surface with a halide brine having reduced corrosion effects, the method comprising:
providing a solution comprising a dissolved salt of magnesium chloride, and an anticorrosion agent comprising an alcohol diglycinate; and
applying the solution to the surface.
9. The method of claim 8 , wherein the solution is applied to the surface in an amount effective to prevent ice formation on the surface.
10. The method of claim 8 , wherein the solution is applied to the surface in an amount effective to suppress dust from blowing off the surface.
11. The method of claim 8 , wherein the alcohol diglycinate has the chemical formula:
where n=1-5, and X and Y are, independently, alkali metal cations.
12. The method of claim 8 , wherein the alcohol diglycinate is a ethanoldiglycinate disodium salt.
13. The method of claim 8 , wherein the concentration of the dissolved salt of magnesium chloride in the solution is about 5% to about 30%, by wt.
14. The method of claim 8 , wherein the concentration of the anticorrosion agent in the solution is about 0.1%, by wt., or more.
15. The method of claim 8 , wherein the concentration of the anticorrosion agent in the solution is about 0.1% to about 0.5%, by wt.
16. A method of treating a transportation surface with a deicing composition to slow the formation of ice and snow on the surface, the method comprising:
providing the deicing composition comprising an aqueous solution of magnesium chloride, and an ethanoldiglycinate disodium salt; and
spraying the deicing composition to the transportation surface in an amount effective to slow the formation of ice and snow on the surface.
17. The method of claim 16 , wherein the concentration of the magnesium chloride comprises about 5% to about 30%, by wt, of the aqueous solution.
18. The method of claim 16 , wherein the concentration of the ethanoldiglycinate disodium salt comprises about 0.1% to about 0.5%, by wt, of the aqueous solution.
19. The method of claim 16 , wherein the deicing composition reduces a corrosion rate by about 70% or more compared with a sodium chloride solution that lacks the ethanoldiglycinate disodium salt.