Optical part holding member and production method thereof
View Patent ↗The present invention relates to an optical part holding member made of ceramic and a production method thereof, and provides an effective permeability to prevent dew condensation. The optical part holding member is made of a silicon nitride ceramic base composite material to hold an optical part, which is produced through a process of nitriding in which silicon is caused to react with nitrogen. By using the silicon nitride ceramic base composite material containing silicon carbide and an iron compound, an airflow volume of 50 ml or more per minute is achieved in an effective airflow area of 1.5 cm 2 when an air pressure is added with a pressure difference of 0.4 MPa between both surfaces of a sample of the silicon nitride ceramic base composite material having 1 mm thickness, and the optical part holding member having effective permeability to prevent dew condensation is obtained.
1. An optical part holding member made of a silicon nitride ceramic base composite material to hold an optical part, wherein silicon carbide and an iron compound are contained in the silicon nitride ceramic base composite material, and an airflow volume per minute is 50 ml or more in an effective airflow area of 1.5 cm 2 when an air pressure is added with a pressure difference of 0.4 MPa between both surfaces of a sample having a 1 mm thickness of the silicon nitride ceramic base composite material.
2. The optical part holding member according to claim 1 , wherein the iron compound contained in the silicon nitride ceramic base composite material is iron silicide.
3. A method of producing an optical part holding member, wherein the optical part holding member includes a silicon nitride ceramic base composite material that is produced through a process of, with respect to silicon powder, mixing silicon carbide powder and iron oxide powder to obtain a mixed powder, producing a molded body by using the obtained mixed powder, and nitriding through a reaction with nitrogen, and
silicon carbide and an iron compound are contained in the silicon nitride ceramic base composite material, and an airflow volume per minute is 50 ml or more in an effective airflow area of 1.5 cm 2 when an air pressure is added with a pressure difference of 0.4 MPa between both surfaces of a sample having a 1 mm thickness of the silicon nitride ceramic base composite material.
4. The method of producing the optical part holding member according to claim 3 , wherein when the mixed powder is produced, iron oxide Fe 3 O 4 powder is added such that the Fe 3 O 4 powder is less than 10 mass % of a total amount of the silicon powder and the silicon carbide powder, and the thus obtained mixed power is used.
5. The method of producing the optical part holding member according to claim 3 , wherein when the mixed powder is produced, iron oxide Fe 3 O 4 powder is added to the silicon powder such that the Fe 3 O 4 powder is equal to or less than 5 mass % of a total amount of raw material powder in which 30 mass % of the silicon carbide powder is added to the silicon powder, and the thus obtained mixed power is used.
6. The method of producing the optical part holding member according to claim 3 , wherein the molded body is produced by injection molding with the use of the mixed powder.
7. The method of producing the optical part holding member according to claim 4 , wherein the molded body is produced by injection molding with the use of the mixed powder.
8. The method of producing the optical part holding member according to claim 5 , wherein the molded body is produced by injection molding with the use of the mixed powder.