Mixtures of nanoparticles
Methods of sol-gel processing for the preparation of mixed gels and nanoparticles are described. Further, mixed gels and nanoparticles obtained by the method are also disclosed. More specifically, a process for mixture of NiO nanoparticles and Yttria stabilized Zirconia nanoparticles obtained by only one sol-gel process is described.
1. A method of sol-gel processing for the preparation of nanoparticles, comprises the steps of:
a) preparing a first aqueous solution comprising at least two inorganic metal salts and a doping agent, and preparing a second aqueous solution comprising pectin and mono or disaccharides;
b) mixing the first and second solutions to form a third solution, at a temperature from about 100-110° C.;
c) incubating the third solution at an elevated temperature of about 100 to 110° C. for sufficient time in order to gelatinize the third solution to a gelatinized material;
d) thermal treatment of the gelatinized material from step c) at a temperature of from 500 to 1200° C., in order to obtain a powder of nanoparticles.
2. The method according to claim 1 , wherein the nanoparticles are monodisperse.
3. The method according to claim 1 , wherein the nanoparticles are less than 150 nanometer in at least one dimension.
4. The method according to claim 1 , wherein the at least two inorganic metal salts contains at least one metal selected from the group consisting of aluminum, hafnium, silicon, zirconium, cerium, lanthanum, germanium, tantalum, nickel and titanium.
5. The method according to claim 1 , wherein the at least two inorganic metal salts contains zirconium salt.
6. The method according to claim 5 , wherein the zirconium salt is a salt selected from the group consisting of ZrCl 4 , ZrO(NO 3 ) 3 and ZrOCl 2 .
7. The method according to claim 4 , wherein the at least two inorganic metal salts contains nickel salt.
8. The method according to claim 7 , wherein the nickel salt is selected from the group consisting of NiCO 3 , Ni(COOH) 2 , Ni(NO 3 ) 2 .6H 2 O, NiSO 4 .7H 2 O.
9. The method according to claim 4 , wherein the at least two inorganic metal salts are salts of nickel and zirconium.
10. The method according to claim 1 , wherein the doping agent is a salt selected from the group consisting of Y 2 O 3 , CaO, MgO, Pr 2 O 3 , Nd 2 O 3 , Sc 2 O 3 and Gd 2 O 3 .
11. The method according to claim 10 , wherein the doping agent is a salt containing yttrium.
12. The method according to 11 , wherein the salt is Y(NO 3 ) 3 .6H 2 O.
13. The method according to claim 1 , wherein the at least two inorganic metal salts are salts of nickel and zirconium, and the doping agent is a salt of Yttrium.
14. The method according to claim 1 , wherein said mono or disaccharides is at least a compound selected from the group consisting of sucrose, maltose, lactose, fructose and glucose.
15. The method according to claim 14 , wherein the mono or disaccharide is sucrose, or a mixture of sucrose and other mono or disaccharides.
16. The method according to claim 1 , wherein the second solution contains sucrose and pectin.