In a process for dropletizing a liquid by means of a dropletizer plate at least the underside of the dropletizer plate has at least in part a contact angle of at least 60° with regard to the liquid to be dropletized.
1. A process for dropletizing a monomer solution to be polymerized by means of a dropletizer plate wherein at least an underside of the dropletizer plate has at least in part a contact angle of at least 60° with regard to the monomer solution.
2. The process according to claim 1 wherein the dropletizer plate at least in part is coated with a material having a contact angle of at least 60° with regard to the monomer solution.
3. The process according to claim 2 wherein the material having a contact angle of at least 60° with regard to the monomer solution is a fluorous polymer.
4. The process according to claim 1 that utilizes a dropletizer plate having drilled holes, whose drilled holes have a diameter in the range from 50 to 1000 μm.
5. The process according to claim 1 wherein the monomer solution is a solution comprising a partially neutralized aqueous acrylic acid.
6. The process according to claim 1 wherein a reactor into which the monomer solution is dropletized has a temperature in the range from 70 to 250° C.
7. The process according to claim 1 wherein the monomer solution is dropletized into an inert gas atmosphere.
8. The process according to claim 1 , wherein the monomer solution is polymerized to provide water-absorbing polymeric particles.
9. The process according to claim 1 wherein the dropletizer plate at least in part is prepared from a material having a contact angle of at least 60° with regard to the monomer solution.
10. The process according to claim 9 wherein the material having a contact angle of at least 60° with regard to the monomer solution is a fluorous polymer.
11. The process according to claim 1 wherein the monomer solution is an aqueous monomer solution.
12. The process according to claim 1 wherein the monomer solution is dropletized in a form of monodisperse droplets.
13. The process of claim 1 wherein the dropletizer plate further comprises a carrier plate having drilled holes of larger diameter than drilled holes in the dropletizer plate, and positioned under the dropletizer plate such that each drilled hole of the dropletizer plate is above a concentric drilled hole in the carrier plate.