High strength aluminum alloy fin material and method of production of same

Assignee: Nippon Light Metal Company, Ltd.
View Patent ↗
Loading inventors, assignments & file history…
Monitor This Case
Get email alerts when status or documents change.
Order Certified Copies
Most orders are placed with the USPTO same day — all within 24 business hours.
Order via The Patent Place →
Pre-filled with this patent's details
Quick Facts
Patent No.
US 7,998,288
App. No.
11/996,836
Granted
Aug 16, 2011
Kind
B2
Abstract

A heat exchanger use high strength aluminum alloy fin material having a high strength and excellent in thermal conductivity, erosion resistance, sag resistance, sacrificial anodization effect, and self corrosion resistance, characterized by containing Si: 0.8 to 1.4 wt %, Fe: 0.15 to 0.7 wt %, Mn: 1.5 to 3.0 wt %, and Zn: 0.5 to 2.5 wt %, limiting the Mg as an impurity to 0.05 wt % or less, and having a balance of ordinary impurities and Al in chemical composition, having a metal structure before brazing of a fibrous crystal grain structure, a tensile strength before brazing of not more than 240 MPa, a tensile strength after brazing of not less than 150 MPa, and a recrystallized grain size after brazing of 500 μm or more.

Claims (4)

1. A method of producing a heat exchanger use high strength aluminum alloy fin material containing Si: 0.8 to 1.4 wt %, Fe: 0.15 to 0.7 wt %, Mn: 1.5 to 3.0 wt %, and Zn: 0.5 to 2.5 wt %, limiting the Mg as an impurity to 0.05 wt % or less, and having a balance of ordinary impurities and Al in chemical composition, having a metal structure before brazing of a fibrous crystal grain structure, a tensile strength before brazing of not more than 240 MPa, a tensile strength after brazing of not less than 150 MPa, and a recrystallized grain size after brazing of 1800 μm or more, comprising casting a melt having the chemical composition above so as to continuously cast and coil into a roll a thin slab having a thickness of 5 to 10 mm by a twin-belt casting machine, cold rolling the slab to a sheet thickness of 1.0 to 6.0 mm, treating the sheet by primary intermediate annealing at 200 to 350° C., further cold rolling the sheet to a sheet thickness 0.05 to 0.4 mm, treating the sheet by secondary intermediate annealing performed by a batch annealing furnace with a holding temperature of 360 to 450° C., and cold rolling the sheet by a final cold rolling rate of 10% to less than 50% to a final sheet thickness 40 to 200 μm.

2. A method as set forth in claim 1 , wherein, in the stages of after said primary intermediate annealing, after the secondary intermediate annealing, and after the final annealing, the metal structure is a fibrous crystal grain structure.

3. A method of producing a heat exchanger use high strength aluminum alloy fin material containing Si: 0.8 to 1.4 wt %, Fe: 0.15 to 0.7 wt %, Mn: 1.5 to 3.0 wt %, and Zn: 0.5 to 2.5 wt %, limiting the Mg as an impurity to 0.05 wt % or less, and having a balance of ordinary impurities and Al in chemical composition, having a metal structure before brazing of a fibrous crystal grain structure, a tensile strength before brazing of not more than 240 MPa, a tensile strength after brazing of not less than 150 MPa, and a recrystallized grain size after brazing of 1800 μm or more, comprising casting a melt having the chemical composition above to continuously cast and coil into a roll a thin slab having a thickness of 5 to 10 mm by a twin-belt casting machine, cold rolling the slab to a sheet thickness of 1.0 to 6.0 mm, treating the sheet by primary intermediate annealing, in a continuous annealing furnace with a rate of temperature rise of 100° C./min or more and with a holding temperature of 400 to 500° C. and a holding time of no more than 5 minutes, further cold rolling the sheet to a sheet thickness 0.05 to 0.4 mm, treating the sheet by secondary intermediate annealing at 360 to 450° C., and cold rolling the sheet by a final cold rolling rate of 10% to less than 50% to a final sheet thickness 40 to 200 μm.

4. A method as set forth in claim 3 , wherein, in the stages of after said primary intermediate annealing, after the secondary intermediate annealing, and after a final annealing, the metal structure is a fibrous crystal grain structure.