Composition for etching a metal hard mask material in semiconductor processing
An etching solution for a metal hard mask. The etching solution comprises a mixture of a dilute HF (hydrofluoric acid) and a silicon containing precursor. The etching solution also comprises a surfactant agent, a carboxylic acid, and a copper corrosion inhibitor. The etching solution is selectively toward etching the metal hard mask material (e.g., Titanium) while suppressing Tungsten, Copper, oxide dielectric material, and carbon doped oxide.
1. A wet etching solution capable of selectively etching Titanium comprising:
products of a mixture of a dilute HF (hydrofluoric acid) and a silicon containing precursor selected from the group consisting of Methyltrimethoxysilane, Methyltriethoxysilane (MTES), Tetramethoxysilane (TMOS), Tetraethoxysilane (TEOS), and Tetrapropoxysilane;
a surfactant agent;
a carboxylic acid; and
a copper corrosion inhibitor.
2. The homogeneous wet etching solution of claim 1 , wherein the silicon containing precursor is MTES (Methyltriethoxysilane).
3. The homogeneous wet etching solution of claim 1 , wherein the surfactant agent is selected from the group consisting of alcohols, amines, amides, esters, ketones, aldehydes, carboxylic acids, and ethers.
4. The homogeneous wet etching solution of claim 1 , wherein the copper corrosion inhibitor is selected from the group consisting of Mercaptobenzothiazole, 2-Mercaptobenzimidazole, 5-chlorobenzotriazole, 5-methylbenzotriazole, Benzotriazole, Carboxybenzotriazole, Tolyltriazole, 1-Phenyl-1H-tetrazole-5-thiol, and hexadecyltrimethylammonium bromide.
5. The homogeneous wet etch solution of claim 1 wherein the products comprises silicon fluoride, silicic acid, and water, and the homogeneous wet etching solution has a pH of 1-3.
6. The homogeneous wet etching solution of claim 5 wherein silicon containing precursor has a concentration ranging from 0.001% to 60% by weight of the mixture and the dilute HF has a concentration ranged from 0.0001% to 49% by weight of the mixture.
7. The homogeneous wet etching solution of claim 6 , wherein the silicon containing precursor is MTES (Methyltriethoxysilane).
8. A homogeneous wet etching solution comprising:
products of a mixture of:
a dilute HF (hydrofluoric acid); and
MTES (Methyltriethoxysilane); and
a copper corrosion inhibitor.
9. The homogeneous wet etching solution of claim 8 , wherein a concentration range of the copper corrosion inhibitor is from 0.0001% to 20% by weight of the homogenous wet etching solution.
10. The homogeneous wet etching solution of claim 9 , wherein the mixture consists essentially of the dilute HF and MTES.
11. The homogenous wet etching solution of claim 8 , consisting essentially of the products and the copper corrosion inhibitor.
12. The homogenous wet etching solution of claim 11 , wherein the products comprise silicon fluoride, silicic acid and water, and the homogeneous wet etching solution has a pH of 1-3.
13. The homogenous wet etching solution of claim 12 , wherein the products further comprise an alcohol.
14. The homogenous wet etching solution of claim 13 , wherein the products do not comprise MTES.
15. The homogenous wet etching solution of claim 8 , wherein the products comprise silicon fluoride, silicic acid and water, and the homogeneous wet etching solution has a pH of 1-3.
16. The homogenous wet etching solution of claim 15 , wherein the products further comprise an alcohol.
17. The homogenous wet etching solution of claim 16 , wherein the products do not comprise MTES.