Paste composition for aluminum brazing
View Patent ↗A paste composition for aluminum brazing of the invention contains 40 to 65% by weight of a metal powder for brazing (a), 5 to 35% by weight of a fluoride type flux (b), 1 to 10% by weight of a methacrylic acid ester type polymer (c), and 10 to 40% by weight of an organic solvent (d); and the component (d) is a hydrocarbon type organic solvent having no aromatic ring and no hydroxyl group and the composition is in a paste-like state having a viscosity of 6,000 to 200,000 mPa·s at 23° C. and accordingly, the storage stability and applicability (practically, discharge property and pressure stability by using a dispenser) and brazing property can be improved in good balance.
1. A paste composition for aluminum brazing comprising
40 to 65% by weight of a metal powder for brazing (a),
5 to35% by weight of a fluoride type flux (b),
1 to 10% by weight of a methacrylic acid ester type polymer (c), and
10 to 40% by weight of an organic solvent (d),
wherein the organic solvent (d) is a naphthene type alicyclic hydrocarbon having no aromatic ring and no hydroxyl group, where the naphthene type alicyclic hydrocarbon type organic solvent has a boiling point of 150° C. or higher, the methacrylic acid ester type polymer(c) is a polymer selected from the group consisting of homopolymers of C 1 to C 18 alkyl esters of methacrylic acid and copolymers of C 1 to C 18 alkyl esters of methacrylic acid and hydroxyl group-containing methacrylic acid esters, where the hydroxyl group-containing methacrylic acid esters have neither a carboxyl group nor a sulfonic acid group, and the composition is a paste-like state having a viscosity of 6,000 to 200,000mPa · at 23° C.
2. The paste composition for aluminum brazing according to claim 1 , wherein the weight average molecular weight of the methacrylic acid ester type polymer (c) is 500,000 to 2,000,000.
3. The paste composition for aluminum brazing according to claim 1 , further comprising a thickener.
4. The paste composition for aluminum brazing according to claim 3 , wherein the thickener is at least one selected from the group consisting of a fatty acid amide type thickener and a hardened caster oil type thickener.
5. The paste composition for aluminum brazing according to claim 3 , wherein the content of the thickener is 0.1 to 5% by weight in the composition.
6. The paste composition for aluminum brazing according to claim 1 , wherein the metal powder for brazing (a) is at least one selected from a group consisting of metal silicon, a silicon-aluminum alloy, a silicon-zinc alloy, a silicon-aluminum-zinc alloy, a silicon-magnesium alloy, a silicon-aluminum-magnesium alloy, a silicon-copper alloy, a silicon-aluminum-copper alloy, and aluminum-zinc alloy.
7. The paste composition for aluminum brazing according to claim 1 , wherein the fluoride type flux (b) is at least one selected from the group consisting of potassium fluoroaluminate, potassium fluoride, aluminum fluoride, lithium fluoride, sodium fluoride, potassium fluoroaluminate-cesium complex, cesium fluoroaluminate, potassium fluorozincate, and cesium fluorozincate.
8. A method for brazing a member made of aluminum, comprising applying the paste composition for aluminum brazing according to any one of claims 1 , 2 , and 3 to 7 to the member and heating the member in a state that the member is assembled in a prescribed structure.