Process for production of fluorine-containing polymers and fluorine-containing polymers
A method of producing a fluoropolymer by which a melt-processable fluoropolymer (A) having a specific unstable terminal group or groups (P) is subjected to melt-kneading in a kneader having a stabilization treatment zone to thereby produce a fluoro-polymer (B) resulting from conversion of the specific unstable terminal group or groups (P) to —CF 2 H. The specific unstable terminal group or groups (P) include alkoxycarbonyl groups, fluoroalkoxycarbonyl groups and/or carboxyl group quaternary nitrogen compound salts, the melt-kneading is carried out in the absence or presence of an alkali metal element or alkaline earth metal element, the content of the alkali metal element or alkaline earth metal element is not greater than 2 ppm of the composition under melt-kneading, and the melt-kneading in the stabilization treatment zone is carried out in the presence of water. A fluoro-polymerised material is also disclosed.
1. A method of producing a fluoropolymer by which a melt-processable fluoropolymer (A) having a specific unstable terminal group or groups (P) is subjected to melt-kneading in a kneader comprising a stabilization treatment zone to thereby produce a fluoropolymer (B) resulting from conversion of said specific unstable terminal group or groups (P) to —CF 2 H,
said specific unstable terminal group or groups (P) comprising alkoxycarbonyl groups and/or fluoroalkoxycarbonyl groups,
the melt-kneading being carried out in the absence or presence of an alkali metal element or alkaline earth metal element,
the content of said alkali metal element or alkaline earth metal element being not greater than 2 ppm of the composition under melt-kneading, and
the melt-kneading in said stabilization treatment zone being carried out in the presence of water.
2. The method of producing a fluoropolymer according to claim 1 , wherein the melt-kneading in the stabilization treatment zone is carried out in the presence of oxygen gas.
3. The method of producing a fluoropolymer according to claim 1 , wherein the kneader is a screw-type extruder.
4. The method of producing a fluoropolymer according to claim 3 , wherein the screw-type extruder is a twin-screw extruder.
5. The method of producing a fluoropolymer according to claim 1 , wherein the temperature in the stabilization treatment zone is set at 280 to 430° C.