Polycarbonate for making extruded films that are virtually free of surface defects
Linear polycarbonate resin virtually free of surface defects that impair the suitability of the resin for demanding optical application is disclosed. Also disclosed is a process for the manufacture of the resin. The surface defects included in the resin are in the form of transparent fluorescing particles, the particle count of which portion that are 15 and 250 μm in size, is up to 1.8 counts/g, said count being determined by exciting the residue remaining after filtering a solution of said polycarbonate in methylene chloride through a Teflon filter of 5 μm pore size at a wavelength of 400-440 nm, 25× overall magnification and illumination time of 40 millisec. The polycarbonate is suitable for making films of improved optical properties.
1. In the continuous interfacial polymerization process for producing polycarbonate, the improvement comprising isolating the polycarbonate in three flash stages and an evaporation extruder, characterized in that the temperature in the first flash stage is 70 to 80° C. at 0.35-0.45 bar excess pressure and the temperature in the second flash stage is 125 to 135° C. at 0.75-0.85 bar excess pressure, and the temperature in the third flash stage is 175 to 185° C. at 1.85-1.95 bar excess pressure.
2. The process according to claim 1 , wherein the temperature difference between any two consecutive flash stages does not exceed 60° C.
3. The process according to claim 1 , further comprising a filtration step coupled with an automated evaluation step to isolate the fluorescing particles and classifies them in order of size.
4. The process according to claim 1 , wherein the polycarbonate produced is a linear polycarbonate resin comprising transparent fluorescing particles having a particle count of up to 1.8 counts/g of particles that are between 15 and 250 μm in size, said count being determined by exciting the residue remaining after filtering a solution of said polycarbonate in methylene chloride through a Teflon filter of 5 μm pore size at a wavelength of 400 to 440 nm, 25× overall magnification and illumination time of 40 millisec.
5. The process according to claim 4 , wherein the particle count of particles having a diameter greater than 120 μm is not more than 0.02 count/g.
6. A process for producing a polycarbonate with a particle count of 0.1 to 1.8 counts/g of fluorescing particles having a diameter of between 15 and 250 μm, comprising
a) producing a linear polycarbonate;
b) determining the particle count of fluorescing particles of size between 15 and 250 μm;
c) repeating a) and b) while manipulating one or more process parameters of residence time, pressure or temperature, until a particle count of 0.1 to 1.8 counts/g of fluorescing particles having a diameter of between 15 and 250 μm is obtained in b).
7. The process according to claim 6 , wherein in c), the particle count of particles having a particle diameter of greater than 120 μm does not exceed 0.02 count/g.
8. The process according to claim 6 , wherein in b), the determination of the particle count is carried out by dissolving the polycarbonate in methylene chloride and filtering through a Teflon filter of 5 μm pore size at an excitation wavelength of 400 to 440 nm and a 25× overall magnification with an illumination time of 40 millisec.
9. The process according to claim 6 , wherein the linear polycarbonate is produced by a process which comprises isolating a polycarbonate in three flash stages and an evaporation extruder, characterized in that the temperature in the first flash stage is 70 to 80° C. at 0.35-0.45 bar excess pressure and the temperature in the second flash stage is 125 to 135° C. at 0.75-0.85 bar excess pressure, and the temperature in the third flash stage is 175 to 185° C. at 1.85-1.95 bar excess pressure.