Sparkle effect of unique particle size distribution
An effect pigment formed from a synthetic platelet substrate such as glass flake has improved sparkle by reducing the amount of substrate particles having a size of less than 9 microns and greater than 85 microns. The present effect pigment is useful in cosmetics, personal care products, and industrial applications such as automotive paints.
1. An effect pigment comprising a synthetic platelet coated with a translucent metal oxide film, said synthetic platelet having a size distribution characterized as a D10 of at least 9.5 microns, a D50 of between about 20 and less than 40 microns, and a D90 of over 35 to less than 85 microns.
2. The effect pigment of claim 1 wherein said size distribution is a substantially Gaussian distribution.
3. The effect pigment of claim 1 wherein said synthetic platelet substrate comprises glass flakes.
4. The effect pigment of claim 1 wherein said metal oxide film comprises titanium dioxide.
5. The effect pigment of claim 1 wherein said metal oxide film comprises iron oxide.
6. The effect pigment of claim 3 wherein said metal oxide film comprises titanium dioxide.
7. The effect pigment of claim 3 wherein said metal oxide film comprises iron oxide.
8. The effect pigment of claim 1 having a D10 of about 9.5 microns, a D50 of about 22 microns, and a D90 of about 45 microns.
9. The effect pigment of claim 1 wherein said synthetic platelet is selected from aluminum oxide, silicon dioxide, bismuth oxychloride, boron nitride, and glass.
10. The effect pigment of claim 9 wherein said metal oxide is titanium dioxide, iron oxide, zirconium oxide, chromium oxide, nickel oxide, cobalt oxide, tin oxide, or combinations thereof.
11. The effect pigment of claim 4 comprising from about 2.5 to 10% by weight TiO 2 .
12. The effect pigment of claim 11 wherein said synthetic platelet is glass flake.
13. A plastic colored with the effect pigment of claim 1 .
14. A cosmetic colored with the effect pigment of claim 1 .
15. A paint suitable for automobiles colored with the effect pigment of claim 1 .
16. The paint of claim 15 wherein said metal oxide is selected from the oxides of titanium, iron, or mixtures thereof.
17. The paint of claim 15 wherein said synthetic platelet is glass flake.
18. The paint of claim 15 wherein the size distribution of said synthetic platelet comprises a D10 of about 9.5 microns, a D50 of about 22 microns, and a D90 of about 45 microns.
19. The paint of claim 17 wherein said metal oxide is selected from the oxides of titanium and/or iron.
20. The paint of claim 15 wherein said platelet substrate is selected from aluminum oxide, silicon dioxide, bismuth oxychloride, boron nitride, and glass.