Electrically conductive fiber and brush
There is provided a conductive fiber containing a conductive substance, and having stable conductive performance with a small variation in its conductive performance. A conductive fiber contains carbon black as a main conductive component in a fiber-forming polymer, wherein the carbon black is composed of a mixture of at least two kinds of the following carbon blacks (A) and (B), which is obtained by mixing them at an A/B ratio (by weight) of 90/10 to 10/90: (A) a conductive carbon black having an average particle size of 20 to 70 nm and an oil absorption defined in JIS K 5101 of 100 to 600 ml/100g; and (B) a conductive carbon black in which the average article size ratio thereof to said conductive carbon black (A) is from 1.1 to 3, and the oil absorption ratio thereof to said conductive carbon black (A) is from 0.9 to 0.2.
1. A conductive fiber containing carbon black as a main conductive component in a fiber-forming polymer, wherein the carbon black is composed of a mixture of at least two kinds of the following carbon blacks (A) and (B), which is obtained by mixing them at an A/B ratio (by weight) of 90/10 to 10/90:
(A) A conductive carbon black having an average particle size of 20 to 70 nm and an oil absorption defined in JIS K 5101 of 100 to 600 ml/100 g; and
(B) A conductive carbon black in which the average article size ratio thereof to said conductive carbon black (A) is from 1.1 to 3, and the oil absorption ratio thereof to said conductive carbon black (A) is from 0.9 to 0.2,
wherein the mixture of at least two kinds of carbon blacks (A) and (B) is homogeneously blended with the fiber forming polymer acting as a matrix component in an amount of 10 to 35% by weight to form the whole cross section of the fiber as a conductive component.
2. The conductive fiber according to claim 1 , wherein the cross-sectional resistance value is from 10 8 to 10 12 Ω/cm.
3. A brush using the conductive fiber according to claim 2 .
4. A brush using the conductive fiber according to claim 1 .
5. A conductive fiber containing carbon black as a main conductive component in a fiber-forming polymer, wherein the carbon black is composed of a mixture of at least two kinds of the following carbon blacks (A) and (B), which is obtained by mixing them at an A/B ratio (by weight) of 90/10 to 10/90:
(A) A conductive carbon black having an average particle size of 20 to 70 nm and an oil absorption defined in JIS K 5101 of 100 to 600 ml/100 g; and
(B) A conductive carbon black in which the average article size ratio thereof to said conductive carbon black (A) is from 1.1 to 3, and the oil absorption ratio thereof to said conductive carbon black (A) is from 0.9 to 0.2,
wherein the cross-sectional resistance value is from 10 8 to 10 12 Ω/cm,
wherein the conductive fiber is a sheath-core type composite fiber, and
wherein the sheath component contains the mixture of at least two kinds of carbon blacks (A) and (B) in an amount of 10 to 35% by weight.
6. A brush using the conductive fiber according to claim 5 .