UV-curable undercoat
A UV-curable undercoat that contains barium sulfate, production thereof, methods of coating substrates with the undercoat and the coated substrates.
1. A UV-curing primer comprising barium sulfate having an average particle size of 10 to 120 nm, a binder, an UV initiator, and a reactive thinner, wherein the binder is from 40 to 80 wt. %, the reactive thinner is from 20 to 45 wt. %, the UV initiator is from 2 to 10 wt. %, and the barium sulfate is from 1 to 25 wt. %.
2. An UV-curing primer according to claim 1 , wherein the binder comprises a compound with one or more UV-curing acrylate or methacrylate function.
3. An UV-curing primer according to claim 1 , wherein the binder comprises at least one member selected from the group consisting of an epoxy acrylate, a polyurethane acrylate, a melamine acrylate, a polyester acrylate, a polyether acrylate, a silicone acrylate, an epoxy methacrylate, a polyurethane methacrylate, a melamine methacrylate, a polyester methacrylate, a polyether methacrylate, a silicone methacrylate, an unsaturated acrylic resin, an unsaturated methacrylic resin and a polyester resin.
4. An UV-curing primer according to claim 1 , wherein the reactive thinners comprises at least one of styrene, a mono-functional acrylate, a di-functional acrylate, a tri-functional acrylate, a tetra-functional acrylate, a mono-functional methacrylate, a di-functional methacrylate, a tri-functional methacrylate or a tetra-functional methacrylate.
5. An UV-curing primer according to claim 1 , wherein the UV initiator comprises at least one of benzophenone, benzoin ether, benzil, a benzine ketal, α-hydroxyalkylphenone, α-aminoalkylphenone, a benzoyl phosphine oxide or a derivative thereof.
6. An UV-curing primer according to claim 1 , comprising an adhesion promoter.
7. An UV-curing primer according to claim 1 , further comprising at least one of an inorganic or an organic colorant.
8. An UV-curing primer according to claim 1 , further comprising an anti-corrosive pigment wherein the anti-corrosive pigment is an organic inhibitors or an inorganic anti-corrosive pigment.
9. A process for the production of a UV-curing primer according to claim 1 wherein the barium sulfate is admixed with a coating composition comprising an acrylate.
10. A process according to claim 9 , wherein the particle size range of barium sulfate is from 30 to 80 nm.
11. A UV-curing primer prepared by the process of claim obtainable according to claim 10 .
12. A process comprising coating a surface with a UV-curing primer according to claim 1 and UV curing the coating to form a cured coating on the surface.
13. A process according to claim 12 , wherein the surface is metallic.
14. A coated substrate coated with the UV-curing primer according to claim 1 , wherein the coating is cured with UV radiation.
15. The coated substrate of claim 14 , which is a metal coil, a can or a container.
16. The coated substrate of claim 14 , wherein the substrate is pretreated with an inorganic chemical for corrosion protection.
17. The coated substrate of claim 14 , wherein the substrate is planar.
18. The coated substrate of claim 14 , wherein the substrate is pretreated with an organic chemical for corrosion protection.
19. The UV-curing primer of claim 1 , wherein the particle size range is from 20 to 100 nm.
20. The UV-curing primer of claim 19 , wherein the particle size range is from 30 to 80 nm.
21. The UV-curing primer of claim 19 , wherein the particle size range is from 40 to 60 nm.
22. The UV-curing primer of claim 1 , further comprising at least one of a an additive, a colored pigment or an anti-corrosive agent.