Composite guide wire with drawn and filled tube construction
The present invention is directed to an intracorporeal device, preferably a guidewire, and method for making the device. The guidewire of the present invention is formed, at least in part, of a composite elongate core formed, at least in part, of precipitation hardened material. The elongate core members of the present invention will have an ultimate tensile strength and modulus of elasticity greater than the same for an identically dimensioned elongate member formed from superelastic NITINOL alone.
1. An intraluminal guidewire, comprising:
a composite elongate core including a precipitation hardenable material and a superelastic nickel-titanium alloy having a ternary element selected from the group consisting of iridium, platinum, gold, rhenium, tungsten, palladium, rhodium, tantalum, silver, ruthenium and halfnium; and
wherein the precipitation hardenable material includes by chemical composition percentage approximately 25 percent molybdenum, 8 percent chromium, 2.5 percent cobalt, a maximum of each of 2 percent iron, 0.8 percent manganese, 0.8 percent silicon, 0.5 percent aluminum, 0.5 percent copper, 0.03 percent carbon and 0.006 percent boron, and a balance of 65 percent nickel.
2. The intraluminal guidewire of claim 1 , wherein the nickel-titanium alloy comprises at least 2.5 atomic percent and less than or equal to 15 atomic percent platinum such that a stress-strain hysteresis curve thereof approximates an idealized stress-strain hysteresis curve of binary nickel-titanium.
3. The intraluminal guidewire of claim 1 , wherein the nickel-titanium alloy comprises at least 2.5 atomic percent and less than or equal to 20 atomic percent palladium such that a stress-strain hysteresis curve thereof approximates an idealized stress-strain hysteresis curve of binary nickel-titanium.
4. The intraluminal guidewire of claim 1 , wherein the superelastic nickel-titanium alloy is comprised of about 30 to about 52 percent titanium, up to 10 percent of one or more ternary elements and the balance nickel.
5. The intraluminal guidewire of claim 4 , wherein the superelastic nickel-titanium alloy is comprised of 42.8 atomic percent nickel, 49.7 atomic percent titanium and 7.5 atomic percent platinum.
6. The intraluminal guidewire of claim 1 , wherein the superelastic nickel-titanium alloy includes a quaternary element.
7. The intraluminal guidewire of claim 6 , wherein the quaternary element is iron.
8. An intraluminal guidewire, comprising:
a composite elongate core, the elongate core having an inner core element and a first layer at least partially covering the inner core element, the inner core element formed from precipitation hardenable material, and the first layer portion formed from a superelastic nickel-titanium alloy including a ternary element selected from the group consisting of iridium, platinum, gold, rhenium, tungsten, palladium, rhodium, tantalum, silver, ruthenium and halfnium; and
wherein the precipitation hardenable material includes by chemical composition percentage approximately 25 percent molybdenum, 8 percent chromium, 2.5 percent cobalt, a maximum of each of 2 percent iron, 0.8 percent manganese, 0.8 percent silicon, 0.5 percent aluminum, 0.5 percent copper, 0.03 percent carbon and 0.006 percent boron, and a balance of 65 percent nickel.
9. The intraluminal guidewire of claim 8 , wherein the composite elongate core includes a distal segment having a distally tapered section with proximal and distal portions, and a distal flexible section, the inner core element being at least partially exposed at the distal flexible section of the distal segment of the composite elongate member.
10. An intraluminal guidewire, comprising:
an inner core element having a length, the inner core element formed from a precipitation hardenable material, wherein the precipitation hardenable material includes by chemical composition percentage approximately 25 percent molybdenum, 8 percent chromium, 2.5 percent cobalt, a maximum of each of 2 percent iron, 0.8 percent manganese, 0.8 percent silicon, 0.5 percent aluminum, 0.5 percent copper, 0.03 percent carbon and 0.006 percent boron, and a balance of 65 percent nickel; and
a layer disposed about the inner core element and extending substantially the length of the inner core element, the layer formed from a nickel-titanium alloy.
11. The intraluminal guidewire of claim 10 , wherein the layer is a first layer portion and further including a second layer portion, the second layer portion formed from the precipitation hardenable material.
12. The intraluminal guidewire of claim 10 , wherein the nickel-titanium alloy includes a ternary element selected from the group consisting of iridium, platinum, gold, rhenium, tungsten, palladium, rhodium, tantalum, silver, ruthenium and halfnium.
13. The intraluminal guidewire of claim 10 , wherein the precipitation hardenable material comprises a nickel-molybdenum-chromium alloy.