Porous nanohybrid materials formed by covalent hybridization between metal-organic frameworks and gigantic mesoporous materials

1. Ultraporous organic-inorganic nanoporous hybrids in which a mesoporous material including organic groups on the surface thereof is covalently-bonded with a crystalline organic-inorganic hybrid, the composite produced by the steps of:

1) mixing an organic precursor for introducing a primary organic functional group, an inorganic precursor and a surfactant to form a mixture and then reacting the mixture to prepare a mesoporous cellular foam (MCF-R) where R is selected from a R1, a primary organic functional group or a R2, a secondary organic functional group;

2) mixing the MCF-R with a solution of a metal-organic framework (MOF) precursor and a nonporous organic-inorganic hybrid (NOIH) precursor to prepare an MCF-R-MOF composite; and

3) crystallizing the MCF-R-MOF composite.

2. The ultraporous organic-inorganic nanoporous composite according to claim 1 , wherein the inorganic precursor includes one or more of a salt or an alkoxide composed of a typical element selected from among silicon (Si), aluminum (Al) and combinations thereof; and a salt or an alkoxide composed of a metal selected from among transition metals and lanthanide metals.

3. The ultraporous organic-inorganic nanoporous composite according to claim 2 , wherein the inorganic precursor includes one or more of a salt or an alkoxide composed of Si; and a salt or an alkoxide composed of a metal capable of being substituted with Si and selected from transition metals selected from among Ti, Fe, Co, V, Cr, Mn, Ti, Ga, Sn, Zr and Y and lanthanide metals selected from among Ce, La and combinations thereof.

4. The ultraporous organic-inorganic nanoporous composite according to claim 1 , wherein the organic precursor for introducing the primary organic functional group is prepared using phosphoric acid (H 3 PO 4 ) or organosilane compounds represented by Chemical Formulae 1 to 4 below:

Si(OR) 4−x R x (0.1 =x= 3)  [Chemical Formula 1]

Si(OR) 4−(x+y) R x Z y (0.1= x+y= 3.9)  [Chemical Formula 2]

Si(OR) 4−x R x Si (0.1= x= 3)  [Chemical Formula 3]

Si(OR) 4−(x+y) R x Z y Si (0.1= x+y= 3.9)  [Chemical Formula 4]

wherein Z is a halogen atom, and R is a substitution group selected from the group consisting of an alkyl group of 1 to 20 carbon atoms, the alkyl group being unsubstituted or substituted with the halogen atom, an alkenyl group, an alkynyl group, a vinyl group, an amino group, an cyano group, and a mercapto group.

5. The ultraporous organic-inorganic nanoporous composite according to claim 1 , wherein a metal precursor of the metal-organic framework (MOF) or the nonporous organic-inorganic hybrid (NOIH) includes one or more compounds of metals selected from the group consisting of period IV transition metals including Ti, V, Cr, Mn, Fe, Co, Ni, Cu and Zn; period V transition metals including Y, Zr, Nb, Mo, Tc, Ru, Rh, Pd, Ag and Cd; period VI transition metals including Lu, Hf, Ta, W, Re, Os, Ir, Pt, Au and Hg; typical elements including magnesium (Mg), lithium (Li), aluminum (Al) and silicon (Si); and lanthanide metals including lanthanum (La), cerium (Ce) and a mixture thereof.

6. The ultraporous organic-inorganic nanoporous composite according to claim 1 , wherein the organic-inorganic hybrid includes an organic ligand selected from the group consisting of —CO 2 − , —CS 2 − , —SO 3 − and —N, the organic ligand having coordination sites.

7. The ultraporous organic-inorganic nanoporous composite according to claim 6 , wherein the organic ligand is a compound including multiple carboxylic acid, multiple carboxylic acid anions, pyridine, imidazolate, or pyrazine.

8. The ultraporous organic-inorganic nanoporous composite according to claim 7 , wherein the multiple carboxylic acid includes benzenedicarboxylic acid, naphthalenedicarboxylic acid, benzenetricarboxylic acid, naphthalenetricarboxylic acid, pyridinedicarboxylic acid, bipyridyldicarboxylic acid, formic acid, oxalic acid, malonic acid, succinic acid, glutaric acid, hexanedicarboxylic acid, or heptanedicarboxylic acid.

9. The ultraporous organic-inorganic nanoporous composite according to claim 1 , wherein the MCF-R is mixed with the metal-organic framework (MOF) precursor using an ultrasonic method, an electromagnetic method, or a reflux method.

10. The ultraporous organic-inorganic nanoporous composite according to claim 1 , wherein the MCF-R-MOF composite is crystallized using an electric heating method, an ultrasonic method, an electromagnetic method or an electrochemical method.

11. A method of separating and storing gas, wherein the ultraporous organic-inorganic nanoporous composite according to claim 1 is formed into a powdered or molded adsorbent, membrane or separating film and then used.

12. The method of separating and storing gas according to claim 11 wherein the gas is hydrogen, oxygen, nitrogen, argon, methane, carbon dioxide or olefin/paraffin mixed gas.

13. The method of separating and storing gas according to claim 11 , wherein the gas is an olefin/paraffin mixed gas selected from the group consisting of ethane/ethene, propane/propylene, butane/butene and butane/isobutene mixtures.

14. A method of producing an ultraporous organic-inorganic nanoporous composite, comprising:

1) mixing an organic precursor for introducing a primary organic functional group, an inorganic precursor, a surfactant and acetic acid to form a mixture and then reacting the mixture to prepare a mesoporous cellular foam (MCF-R) where R is selected from a R1, a primary organic functional group or a R2, a secondary organic functional group;

2) mixing the MCF-R with a solution of a metal-organic framework (MOF) precursor and a nonporous organic-inorganic hybrid (NOIH) precursor to prepare an MCF-R-MOF composite; and

3) crystallizing the MCF-R-MOF composite.