Shaped abrasive particles with an opening
Abrasive particles which are shaped abrasive particles each with an opening is disclosed. The shaped abrasive particles are formed from alpha alumina and have a first face and a second face separated by a thickness t. The opening in each of the shaped abrasive particles can improve grinding performance by reducing the size of a resulting wear flat, can provide a reservoir for grinding aid, and can improve adhesion to a backing in a coated abrasive article.
1. Abrasive particles comprising: shaped abrasive particles having a shape that is replicated from a mold cavity, the shaped abrasive particles each having an opening, each of the shaped abrasive particles comprising alpha alumina and having a first face and a second face separated by a thickness t.
2. The abrasive particles of claim 1 wherein a perimeter of the first face and the second face comprises a triangular shape.
3. The abrasive particles of claim 2 wherein the opening comprises a substantially triangular shape.
4. The abrasive particles of claim 1 wherein the opening passes through the first face and the second face.
5. The abrasive particles of claim 4 comprising an opening ratio of an opening area divided by an area of the larger of either the first face or the second face and wherein the opening ratio is between 0.05 to about 0.95.
6. The abrasive particles of claim 5 wherein the opening ratio is between 0.1 to about 0.5.
7. The abrasive particles of claim 6 wherein a perimeter of the first face and the second face comprises a triangular shape.
8. The abrasive particles of claim 7 wherein the opening comprises a substantially triangular shape.
9. The abrasive particles of claim 1 wherein a bulk density of the shaped abrasive particles is less than 1.35 g/cm 3 .
10. The abrasive particles of claim 9 wherein the bulk density of the shaped abrasive particles is less than 1.00 g/cm 3 .
11. The abrasive particles of claim 1 comprising a sidewall connecting the first face and the second face, and a draft angle α between the second face and the sidewall, and the draft angle α is greater than 90 degrees.
12. The abrasive particles of claim 11 wherein the draft angle α is between about 95 degrees to about 130 degrees.
13. The abrasive particles of claim 1 wherein the opening comprises an inner surface and the inner surface is curved such that a size of the opening in the first face is larger than the size of the opening in the second face.
14. The abrasive particles of claim 1 wherein the opening comprises an inner surface and the inner surface is tapered.
15. The abrasive particles of claim 1 wherein the shaped abrasive particles comprise an integral connection of a plurality of bars joined at their respective ends to form a closed polygon.
16. The abrasive particles of claim 15 wherein a perimeter of the first face and the second face comprises a triangular shape.
17. The abrasive particles of claim 16 wherein the opening comprises a substantially triangular shape.
18. The abrasive particles of claim 15 wherein a bulk density of the shaped abrasive particles is less than 1.35 g/cm 3 .
19. The abrasive particles of claim 18 wherein the bulk density of the shaped abrasive particles is less than 1.00 g/cm 3 .
20. The abrasive particles of claim 15 comprising a sidewall connecting the first face and the second face, and a draft angle α between the second face and the sidewall, and the draft angle α is greater than 90 degrees.
21. The abrasive particles of claim 20 wherein the draft angle α is between about 95 degrees to about 130 degrees.
22. The abrasive particles of claim 1 comprising a binder forming an abrasive article selected from the group consisting of bonded abrasive articles, coated abrasive articles, nonwoven abrasive articles, and abrasive brushes.
23. The abrasive particles of claim 1 comprising a make coat on a major surface of a backing and the shaped abrasive particles adhered to the make coat forming an abrasive layer, the abrasive layer coated with a size coat, and wherein the abrasive layer comprises at least 5 percent by weight of the shaped abrasive particles.
24. The abrasive particles of claim 23 comprising a grinding aid in the opening of at least some of the shaped abrasive particles.
25. The abrasive particles of claim 23 comprising the make coat or the size coat in the opening of at least some of the shaped abrasive particles.
26. A method of making the abrasive particles of claim 1 comprising:
providing a mold having a plurality of cavities, the plurality of cavities comprising polymeric surfaces;
filling the plurality of cavities with a sol-gel, the sol-gel comprising particles that can be converted into alpha alumina in a liquid, the liquid comprising a volatile component;
removing at least a portion of the volatile component from the sol-gel while the sol-gel resides in the plurality of cavities thereby forming a plurality of precursor shaped abrasive particles each having an opening; and
sintering the plurality of precursor shaped abrasive particles.
27. The method of claim 26 wherein the plurality of cavities comprise an upstanding mold element that rises from a bottom of the cavity for producing the opening.
28. Abrasive particles comprising: shaped abrasive particles having a shape that is replicated from a mold cavity, the shaped abrasive particles each having a single opening, each of the shaped abrasive particles comprising alpha alumina and having a first face and a second face separated by a thickness t and wherein the single opening passes through the first face and the second face.
29. The abrasive particles of claim 28 comprising an opening ratio of an opening area divided by an area of the larger of either the first face or the second face and wherein the opening ratio is between about 0.05 to about 0.3.
30. The abrasive particles of claim 28 wherein a bulk density of the shaped abrasive particles is less than 1.20 g/cm 3 .
31. The abrasive particles of claim 28 comprising a sidewall connecting the first face and the second face, and a draft angle α between the second face and the sidewall, and the draft angle α is greater than 90 degrees.
32. The abrasive particles of claim 28 wherein the shaped abrasive particles comprise an integral connection of a plurality of bars joined at their respective ends to form a closed polygon.
33. The abrasive particles of claim 28 wherein the single opening is selected to have a shape that is different from a shape of a perimeter of the shaped abrasive particles.
34. The abrasive particles of claim 28 wherein a perimeter of the first face and the second face comprises a triangular shape.