Process for producing plastic foam composite
Plastic foam has excellent heat insulation properties, however, moisture absorption is causing a decrease in the heat insulation, and plastic foam has almost no mechanical strength. Therefore, a heat insulation material that absorbs almost no moisture and has satisfactory strength is desired to appear. According to the present invention, a foam composite with a skin can be formed in one shot by charging plastic powders or minute particles together with polyolefin pellets that can be cross-linked and foamed in a mold, and heating the mold while rotating. The composite absorbs almost no moisture, having satisfactory strength, being excellent as an insulating material. Further, providing a covering of a non-foaming or a slightly foaming material to the pellet of polyolefin that can be cross-linked and foamed, and conducting the forming, foamed granules of preferably 5 to 50 mm largeness as a core, and a covering of a reinforcing member with 0.05 to 0.5 mm thickness for the core, can be formed, which permits that thus obtained shaped body is lightweight, strong, with an equivalent strength to wood that undergoes deformation without breaking when subjected to impact.
1. A process for producing a foam composite having a skin with an even thickness and a core comprising foamed bodies with homogeneous and fine bubbles and spherical plastic reinforcing members with an even thickness covering each of the foamed bodies, comprising:
charging a mold with one of plastic powders and plastic minute particles, and polyolefin pellets that are larger than the one of the plastic powders and the plastic minute particles, wherein the polyolefin pellets are covered in the whole surface with plastic and are cross-linkable and foamable; and
heating the mold from the outside of the mold;
rotating the mold at within a range from 1 to 20 rpm, so that a plastic skin is formed and the pellets adhere to the skin; and
further heating the mold, thereby permitting the polyolefin cross-links and the pellets to expand by the decomposition of a foaming agent,
wherein
the thickness of the skin is within a range from 1 to 10 mm;
a number of the foamed bodies, which are bonded each other to constitute the core, are formed from the polyolefin pellets;
a number of the foamed bodies are connected in three dimensions;
the density of the foamed bodies is from 0.1 to 0.01 g/cm 3 ;
the thickness of the core is from 10 to 100 mm; and
the thickness of the foam composite is 25 mm or more,
and wherein the polyolefin pellets are formed by
covering a rod of polyolefin with plastic;
compressing the rod of polyolefin in a molten state to a thickness of plastic in a bonded region of 0.3 mm or more;
cutting the rod of polyolefin;
bonding edge sections of the rod of polyolefin, thereby obtaining pellets with a covering of the plastic in the whole polyolefin surface to form the polyolefin pellets; and
foaming the polyolefin pellets, thereby permitting the foam composite to have a skin with an even thickness and a core, in which nearly even size granular foamed bodies with a covering of a reinforcing member with practically even thickness are integrated, bonded mutually, filling in the core, and further, bonded to the skin.
2. The process for producing a foam composite according to claim 1 , wherein the diameter of the foamed bodies is from 5 to 25 mm and the thickness of the spherical reinforcing members is from 0.05 to 0.5 mm.
3. The process for producing a foam composite according to claim 1 , wherein the plastic powders and the plastic minute particles contain a foaming agent within a range from 1 to 10 PHR.
4. The process for producing a foam composite according to claim 1 , wherein the plastic used for covering the polyolefin that can be cross-linked and foamed contains a foaming agent within a range from 1 to 10 PHR.
5. The process for producing a foam composite according to claim 1 , wherein the quantity of the plastic pellets used is adjusted so that a hollow section with a similar figure to the foam composite is provided in the center thereof.
6. The process for producing a foam composite according to claim 1 , wherein one of rubber waste, plastic waste, composite material waste and the foam composite waste is crushed, and the mold is charged with the crushed waste, permitting the waste to be enclosed inside.
7. The process for producing a foam composite according to claim 1 , wherein the plastic powders or the plastic minute particles is one of high density polyethylene, polypropylene, nylon, and a mixture thereof.
8. The process for producing a foam composite according to claim 1 , wherein the plastic used for covering the polyolefin that can be cross-linked and foamed is one of high density polyethylene, polypropylene, nylon, and a mixture thereof.
9. The process for producing a foam composite according to claim 1 , wherein flame retardant plastic is used as the plastic powders or the plastic minute particles, or a flame retardant is added to the plastic powders and the plastic minute particles.
10. The process for producing a foam composite according to claim 1 , wherein the foam composite has metal fittings inside, and the fittings are secured strongly with both the skin and the reinforcing members.
11. The process for producing a foam composite according to claim 1 , wherein the plastic powders and the plastic minute particles contain one of polyethylene and ethylene-vinyl acetate copolymer, and an organic peroxide within a range from 0.2 to 2.0 PHR.
12. A process for producing a foam composite having a skin with an even thickness and a core comprising foamed bodies with homogeneous and fine bubbles and spherical plastic reinforcing members with an even thickness covering each of the foamed bodies, comprising:
charging a mold with one of plastic powders and plastic minute particles, and polyolefin pellets that are larger than the one of the plastic powders and the plastic minute particles, wherein the polyolefin pellets are covered in the whole surface with plastic and are cross-linkable and foamable; and
heating the mold from the outside of the mold;
rotating the mold at within a range from 1 to 20 rpm, so that a plastic skin is formed and the pellets adhere to the skin; and
further heating the mold, thereby permitting the polyolefin cross-links and the pellets to expand by the decomposition of a foaming agent,
wherein
the thickness of the skin is within a range from 1 to 10 mm;
a number of the foamed bodies, which are bonded each other to constitute the core, are formed from the polyolefin pellets;
a number of the foamed bodies are connected in three dimensions;
the density of the foamed bodies is from 0.1 to 0.01 g/cm3;
the diameter of the foamed bodies is from 5 to 25 mm;
the thickness of the spherical reinforcing members is from 0.05 to 0.5 mm;
the thickness of the core is from 10 to 100 mm; and
the thickness of the foam composite is 25 mm or more;
and wherein the polyolefin pellets are formed by
extruding a polyolefin, which is cross-linkable and foamable, into a rod of polyolefin with a diameter of 2 to 10 mm;
covering the rod of polyolefin with a plastic, thereby obtaining the rod of polyolefin with a covering of the plastic with a thickness of 0.5 to 5 mm;
compressing the rod of polyolefin in a molten state to have a thickness of plastic in a bonded region of 0.3 mm or more;
cutting the rod of polyolefin; and
bonding edge sections of the rod of polyolefin, thereby obtaining the polyolefin pellets with the covering of the plastic in the whole polyolefin surface.