Electrode materials with high surface conductivity
View Patent ↗The present invention concerns electrode materials capable of redox reactions by electrons and alkali ions exchange with an electrolyte. The applications are in the field of primary (batteries) or secondary electrochemical generators, super capacitors and light modulating system of the super capacitor type.
1. A process for making an alkali-metal ion-reversible electrode material comprising the steps of:
(a) providing an alkali-based complex oxide of the general formula
A a M m Z z O o N n F f wherein:
A comprises an alkali metal selected from the group consisting of lithium, sodium, and potassium;
M comprises at least one transition metal, and optionally at least one non-transition metal, or mixtures thereof;
Z comprises at least one non-metal;
O is oxygen;
N is nitrogen; and
F is fluorine,
where Z and O are such that the alkali-based complex oxide is selected from the group consisting of sulfates, phosphates, silicates, oxysulfates, oxyphosphates, oxysilicates and mixtures thereof;
where a ≧0.1; m, o, and z >0; and n and f ≧0 and selected to ensure electroneutrality in said alkali-based complex oxide;
where said alkali-based complex oxide stabilizes all or part of the transition metal ion of M in its lower oxidation level, not considering 0, and conducts alkali metal ions; and
(b) contacting said alkali-based complex oxide with a carbonaceous precursor under conditions of temperature, time and pressure effective to form a conductive carbon coating on said alkali-based complex oxide,
said conductive carbon coating being in a non-powdery form, substantially homogeneous and covering all or most of the surface with a thin film of carbon that is optimized to give electronic conductivity in said alkali-based complex oxide,
without blocking alkali-ion exchanges at the surface of said alkali-based complex oxide,
and without reducing the transition metal of said alkali-based complex oxide to a metallic state,
the alkali-based complex oxide having mixed electron and alkali-ion conductivity and alkali-ion-exchange capability for use in a battery.
2. The process according to claim 1 , wherein said contacting step is a pyrolysing step carried out under vacuum.
3. The process according to claim 1 , wherein said contacting step is a pyrolysing step carried out under non-oxidizing conditions.
4. The process according to claim 1 , wherein said contacting step is a pyrolysing step carried out under reducing conditions.
5. The process according to claim 1 , wherein said carbonaceous precursor is in solid form, and is selected from the group consisting of a polymer, a solid hydrocarbon, and derivatives and mixtures thereof.
6. The process according to claim 1 , wherein said carbonaceous precursor is in solid form and comprises a polymer, and the contacting step further comprises dispersing a polymer or polymer mixture with said alkali-based complex oxide or with precursors of said alkali-based complex oxide so as to form a dispersion, and pyrolysing the dispersion.
7. The process according to claim 1 , wherein, upon said contacting step, said carbonaceous precursor provides CO effective to form said conductive carbon coating according to the equilibrium reaction:
2CO←→CO 2 +C.
8. The process according to claim 1 , wherein said carbonaceous precursor is in liquid form and is selected from the group consisting of a liquid solution of a polymer, a liquid monomer, a liquid hydrocarbon, and mixtures and derivatives thereof.
9. The process according to claim 1 , wherein said carbonaceous precursor is in gaseous form and is selected from the group consisting of gaseous hydrocarbons, CO, CO precursors, and mixtures thereof.
10. The process according to claim 9 , wherein said carbonaceous precursor in gaseous form comprises hydrogen.
11. The process according to claim 9 , wherein said carbonaceous precursor in gaseous form is formed in situ during the contacting step.
12. The process according to claim 11 , wherein said contacting step is carried out at a temperature lower than 900° C.
13. The process according to claim 9 , wherein said carbonaceous precursor comprises CO and wherein said conditions are effective to form said conductive carbon coating according to the equilibrium reaction:
2CO←→CO 2 +C.
14. The process according to claim 1 , wherein providing said alkali-based complex oxide comprises pyrolysing at least one alkali-based complex oxide precursor under conditions effective to form said alkali-based complex oxide.
15. The process according to claim 1 , wherein said contacting step is carried out by pyrolysing said carbonaceous precursor in the presence of said alkali-based complex oxide or in the presence of alkali-based complex oxide precursors.
16. The process according to claim 15 , wherein said alkali-based complex oxide is selected from the group consisting of LiFePO 4 , LiMnPO 4 and mixtures and solutions thereof.
17. The process according to claim 1 , wherein A comprises lithium.
18. The process according to claim 1 , wherein Z comprises phosphorus.
19. The process according to claim 1 , wherein said conductive carbon coating comprises a thin coating of carbon that covers substantially all of the surface of the alkali-based complex oxide.
20. The process according to claim 1 , wherein said conductive carbon coating comprises a thick coating of carbon.