Method of producing a high security film and high security film produced by said method
The invention relates to a high security film, optionally in the form of a slit thread or a micro tape, which is then inserted into high security paper such as a bank note paper and the like during the paper making process. The invention envisages a novel method of producing such a high security film using a print transfer method, wherein one or more security features are incorporated on one or more indicia including letters, optionally graphics, during such a production process, using multiple printing stations and lamination.
1. A method of producing high security film for incorporating into a security paper such as currency note paper or the like; the method comprising the following steps:
(i) loading a roll of a donor web on an unwinder of a multipass print-coat machine, unwinding and passing the donor web through a set of guide and tension control rolls into a printing zone;
(ii) printing desired indicia on the donor web by passing the donor web through one or more print station(s) containing a solution of adhesive and one or more security element(s);
(iii) drying the donor web with adhesive printed indicia containing security elements by passing the donor web through one or more set of driers for evaporating the solvent contained in the adhesive, leaving a desired selective indicia pattern;
(iv) laminating the donor web containing said adhesive printed selective indicia pattern along with one or more security element(s), with a receiver web by passing the donor web and receiver web through nip/press rolls;
(v) rewinding the laminated donor web and receiver web from step (iv) on a rewinder; aging the laminated donor web and receive web by stacking the roll on a stacker for a desired aging period and then splitting/separating out the laminated donor web and receiver web on two different shafts; and
(vi) splitting/separating out the donor web and receiver web, on two different shafts to transfer the adhesive printed selective indicia pattern to the receiver web forming security film.
2. The method according to claim 1 in which the donor web is a hot stamping foil or a holographic foil or a non metallic stamping foil.
3. The method according to claim 1 in which the donor web comprises a first layer of plastic film, a second layer of release coat, a third layer of dye coat and a fourth layer of metallic coat.
4. The method according to claim 3 in which the donor web also includes one or more other layers chosen from the group consisting of tie coats, protective coats, coatings for various effects, and adhesive coats.
5. The method according to claim 3 in which one or more security elements are added in one or more layers of the donor web.
6. The method according to claim 1 in which the printing of the desired indicia on the donor web is carried out at the print station by using gravure cylinder or a flexo etched plate or a web screen system.
7. The method according to claim 1 in which the printing process of donor web with adhesive containing security elements is repeated any number of times in a number of print-coating stations and the security element in the adhesive at each print station can be the same or different depending upon the degree of security required for the security paper.
8. The method according to claim 1 in which the indicia includes any type of texts, graphics or images or a combination thereof printed on the donor web in a desired pattern.
9. The method according to claim 8 in which the indicia printed on the donor web is visible or invisible or machine readable using external readers.
10. The method according to claim 1 in which the adhesive solution used for printing contains resins chosen from the group consisting of acrylics, polyurethane, polyvinyl acetate (PVAC), epoxy resins, and combinations thereof.
11. The method according to claim 1 in which the adhesive used for printing is a water-based adhesive.
12. The method according to claim 1 in which the security elements contained in the adhesive solution used for printing are selected from overt or covert security elements.
13. The method according to claim 1 in which the security elements are either visible, invisible or machine readable using external readers.
14. The method according to claim 1 in which the receiver web is a water soluble film (WSF).
15. The method according to claim 14 , in which the WSF is either a cold water soluble film or a warm water soluble film or a hot water soluble film, the water temperature depending upon the formulations and resins of the WSF and ranges between 5° C. to 100° C.
16. The method according to claim 1 , in which the receiver web is a plastic film.
17. The method according to claim 1 , in which the temperatures at the set of driers used for evaporating the solvent ranges from 30° C. to 190° C.
18. The method according to claim 1 , in which the pressure applied at the nip/press rolls for laminating the two webs ranges from 0.5 psi to 10 psi.
19. The method according to claim 1 , in which reverse printing of the desired indicia is carried out.
20. The method according to claim 1 wherein the said receiver web with security elements is slit into micro tapes and inserted into a paper web during a paper making process.
21. The method according to claim 1 , in which the receiver web with security elements is inserted into a paper web during a paper making process.
22. A method of producing high security film for incorporating into a security paper such as currency note paper or the like; the method comprising the following steps:
(i) loading a roll of a donor web on an unwinder of a multipass print-coat machine, unwinding and passing the donor web through a set of guide and tension control rolls into a printing zone;
(ii) printing desired indicia on the donor web by passing the donor web through one or more print station(s) containing a solution of adhesive and one or more security element(s);
(iii) drying the donor web with adhesive printed indicia containing security elements by passing the donor web through one or more set of driers for evaporating the solvent contained in the adhesive, leaving a desired selective indicia pattern;
(iv) laminating the donor web containing said adhesive printed selective indicia pattern along with one or more security element(s), with a receiver web by passing the donor web and receiver web through nip/press rolls;
(v) rewinding the laminated donor web and receiver web from step (iv) on a rewinder;
(vi) aging the laminated donor web and receiver web by stacking the roll on a stacker for a period ranging from 2 minutes to 72 hours; and
(vii) splitting/separating out the donor web and receiver web, on two different shafts to transfer the adhesive printed selective indicia pattern to the receiver web forming security film.
23. A method of producing high security film for incorporating into a security paper such as currency note paper or the like; the method comprising the following steps:
(i) loading a roll of a donor web on an unwinder of a multipass print-coat machine, unwinding and passing the donor web through a set of guide and tension control rolls into a printing zone;
(ii) printing desired indicia on the donor web by passing the donor web through one or more print station(s) containing a solution of adhesive and one or more security element(s);
(iii) drying the donor web with adhesive printed indicia containing security elements by passing the donor web through one or more set of driers for evaporating the solvent contained in the adhesive, leaving a desired selective indicia pattern;
(iv) laminating the donor web containing said adhesive printed selective indicia pattern along with one or more security element(s), with a receiver web by passing the donor web and receiver web through nip/press rolls;
(v) perforating said receiver web with security elements at selective places;
(vi) inserting the perforated receiver web with security elements into a paper web during a paper making process;
(vii) splitting/separating out the donor web and receiver web, on two different shafts to transfer the adhesive printed selective indicia pattern to the receiver web forming security film.