Durable glass housings/enclosures for electronic devices
The invention relates to glass articles suitable for use as electronic device housing/enclosure or protective cover which comprise a glass material. Particularly, a housing/enclosure/cover comprising an ion-exchanged glass exhibiting the following attributes (1) radio, and microwave frequency transparency, as defined by a loss tangent of less than 0.03 and at a frequency range of between 15 MHz to 3.0 GHz; (2) infrared transparency; (3) a fracture toughness of greater than 0.6 MPa·m 1/2 ; (4) a 4-point bend strength of greater than 350 MPa; (5) a Vickers hardness of at least 450 kgf/mm 2 and a Vickers median/radial crack initiation threshold of at least 5 kgf, (6) a Young's Modulus ranging between about 50 to 100 GPa; (7) a thermal conductivity of less than 2.0 W/m° C., and (9) and at least one of the following attributes: (i) a compressive surface layer having a depth of layer (DOL) greater and a compressive stress greater than 400 MPa, or, (ii) a central tension of more than 20 MPa.
1. An article suitable for housing, enclosing or covering the components of a portable electronic device, the article comprising an ion exchanged alkali-aluminosilicate glass consisting essentially of 64 mol %≦SiO 2 ≦68 mol %; 12 mol %≦Na 2 O≦16 mol %; 8 mol %≦Al 2 O 3 ≦12 mol %; 0 mol % ≦B 2 O 3 ≦3 mol %; 2 mol %≦K 2 O≦5 mol %; 4 mol %≦MgO≦6 mol %; and 0 mol %≦CaO≦5 mol %, wherein: 66 mol %≦SiO 2 +B 2 O 3 +CaO≦69 mol %; Na 2 O+K 2 O +B 2 O 3 +MgO+CaO+SrO>10 mol %; 5 mol %≦MgO+CaO+SrO≦8 mol %; 2 mol %≦Na 2 O−Al 2 O 3 ≦6 mol %; and 4 mol %≦(Na 2 O+K 2 O)−Al 2 O 3 ≦10 mol %, and exhibiting radio and microwave frequency transparency, as defined by a loss tangent of less than 0.03 and at a frequency range of between 15 MHz to 3.0 GHz, infrared transparency, a fracture toughness of greater than 0.60 Mpa·m 1/2 , a 4-point bend strength of greater than 350 MPa, a Vickers hardness of at least 450 kgf/mm 2 , a Vickers median/radial crack initiation threshold of at least 5 kgf, a Young's Modulus ranging between 50 to 100 GPa, a thermal conductivity of less than 2.0 W/m° C. and at least one of the following attributes:
(i) a compressive surface layer having a depth of layer (DOL) greater than or equal to 20 μm and a compressive stress greater than 400 MPa, or,
(ii) a central tension of more than 20 MPa.
2. The article claimed in claim 1 wherein the glass exhibits a refractive index of greater then 1.47 at 633 nm.
3. The article claimed in claim 1 wherein the glass exhibits radio and microwave frequency transparency, as defined by a loss tangent of less than 0.015 at a frequency range of between 500 MHz to 3.0 GHz.
4. The article claimed in claim 1 wherein the glass exhibits a fracture toughness of greater than 0.75 Mpa·m 1/2 .
5. The article claimed in claim 1 wherein the glass exhibits a Young's Modulus ranging between 50 and 75 GPa.
6. The article claimed in claim 1 wherein the glass exhibits an 4-point bend strength of greater than 475 MPa.
7. The article claimed in claim 1 wherein the glass exhibits a Vickers hardness of at least 500 kgf/mm 2 and Vickers median/radial crack initiation threshold of greater than 10 kgf.
8. The article claimed in claim 1 wherein the glass exhibits a thermal conductivity of less than 1.5 W/m° C.
9. The article claimed in claim 1 wherein the glass article is transparent and exhibits at least one surface having a Ra roughness of less than less than 50 nm.
10. The article claimed in claim 1 wherein the glass article appears opaque and exhibits at least one surface having a Ra roughness of between 50 nm and 15 μm.
11. The article as claimed in claim 1 wherein the glass exhibits a near-infra-red transparency of greater than 80% at a wavelength ranging from 750 to 2000 nm.
12. The article as claimed in claim 1 wherein the article exhibits an overall thickness of 1.2 mm and compressive layer exhibiting a DOL of ranging between 40 to 80 μm and the compressive layer exhibits a compressive stress of 525 MPa.
13. The article as claimed in claim 1 wherein the glass exhibits a liquidus viscosity of greater than 130,000 poise at temperatures below 1275° C.
14. The article as claimed in claim 1 wherein the glass is fusion formable and the article is formed by standard processing techniques selected from the group consisting of pressing, sagging, vacuum sagging, sheet coin and combinations thereof.