Holey fiber and method of manufacturing the same

1. A method of manufacturing a holey fiber including a core region and a cladding region surrounding the core region and having air holes arranged around the core region in layers, the method comprising:

forming a preform by arranging a core rod at a center of a jacket tube and arranging capillary tubes having hollows around the core rod inside the jacket tube;

drawing the preform by heat melting the preform in a heating furnace;

determining, during the step of drawing the preform, whether an average of inner diameters of air holes in a first layer from the core region among a plurality of layers of air holes has reached a target value; and

controlling, during the step of drawing the preform, at least one of a gas pressure to be applied to insides of the hollows of the capillary tubes, a temperature of the heating furnace, and a drawing speed, based only on a structure of only the air holes in the first layer from the core region among the plurality of layers of air holes and on the determination of whether the average of the inner diameters of the air holes in the first layer from the core region has reached the target value,

wherein the number of layers of the air holes are three or more, diameters of the air holes are substantially uniform, and intervals between the air holes are substantially uniform.

2. The method according to claim 1 , wherein the drawing includes drawing the preform while controlling gas pressure to be applied to the insides of the hollows of the capillary tubes based on a structure of air holes to be formed in the first layer from the core region.

3. A method of manufacturing a holey fiber including a core region and a cladding region surrounding the core region and having air holes arranged around the core region in layers, the method comprising:

forming a preform by arranging a core rod at a center of a jacket tube and arranging capillary tubes having hollows around the core rod inside the jacket tube; and

drawing the preform by heat melting the preform in a heating furnace, wherein

the drawing includes

preparing capillary tubes;

measuring errors of inner diameters of the capillary tubes from an inner diameter reference value and measuring errors of outer diameters of the capillary tubes from an outer diameter reference value;

selecting a predetermined number of the capillary tubes having errors smaller than a threshold based on the errors measured at the measuring;

arranging the capillary tubes selected at the selecting in a first layer from the core rod,

determining whether an average of inner diameters of air holes in the first layer from the core region among a plurality of layers of air holes has reached a target value; and

controlling at least one of a gas pressure to be applied to insides of the hollows of the capillary tubes, a temperature of the heating furnace, and a drawing speed, based on a structure of only the air holes in the first layer from the core region among the plurality of layers of air holes and on the determination of whether the average of the inner diameters of the air holes in the first layer from the core region has reached the target value,

wherein the number of layers of the air holes are three or more, diameters of the air holes are substantially uniform, and intervals between the air holes are substantially uniform.

4. The method according to claim 3 , wherein the drawing includes drawing the preform while controlling gas pressure to be applied to the insides of the hollows of the capillary tubes based on a structure of the air holes to be formed in the first layer from the core region.

5. The method according to claim 3 , wherein the threshold is an average of the measured errors.