Tough composition for food applications

1. Heterophasic polypropylene composition comprising:

73 to 98 wt.-% of a polypropylene matrix (M) being a propylene homopolymer, and,

2 to 27 wt.-% of an elastomeric copolymer (E) being dispersed in the matrix (M),

based on the polypropylene matrix (M) and the elastomeric copolymer (E)

wherein the elastomeric copolymer (E) comprises units derived from propylene and

ethylene and/or C4 to C20 α-olefin,

and wherein further,

Mz/Mw of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is of more than 2.6, wherein Mz is the z-average molecular weight measured according to ISO 16014-4:2003 and Mw is the weight average molecular weight measured according to ISO 16014-4:2003,

the intrinsic viscosity of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is above 2.1 dl/g measured according to ISO 1628-1 (at 135° C. in decaline),

the MFR 2 (230° C.) of the heterophasic polypropylene composition measured according to ISO 1133 is more than 25 g/10 min, and wherein the amount of propylene derived monomer units in the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is at least 58 wt.-%.

2. Heterophasic polypropylene composition according to claim 1 , wherein

the Mz/Mn of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is below 15.2, and/or

the Mz of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is at least 950 kg/mol,

wherein Mz is the z-average molecular weight measured according to ISO 16014-4:2003 and Mn is the number average molecular weight measured according to ISO 16014-4:2003.

3. Heterophasic polypropylene composition comprising:

73 to 98 wt.-% of a polypropylene matrix (M) being a propylene homopolymer, and,

2 to 27 wt.-% of an elastomeric copolymer (E) being dispersed in the matrix (M), based on the polypropylene matrix (M) and the elastomeric copolymer (E) wherein the elastomeric copolymer (E) comprises units derived from

propylene and

ethylene and/or C4 to C20 α-olefin,

and wherein further,

Mz/Mn of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is below 15.2, wherein Mz is the z-average molecular weight measured according to ISO 16014-4:2003 and Mn is the number average molecular weight measured according to ISO 16014-4:2003,

the Mz of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is at least 950 kg/mol,

the intrinsic viscosity of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is above 2.1 dl/g measured according to ISO 1628-1 (at 135° C. in decaline), and

the MFR 2 (230° C.) of the heterophasic polypropylene composition measured according to ISO 1133 is more than 25 g/10 min, and wherein the amount of propylene derived monomer units in the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is at least 58 wt.%.

4. Heterophasic polypropylene composition according to claim 3 , wherein

the Mz/Mw of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is more than 2.6, wherein Mz is the z-average molecular weight measured according to ISO 16014-4:2003 and Mw is the weight average molecular weight measured according to ISO 16014-4:2003.

5. Heterophasic polypropylene composition according to claim 3 , wherein the weight average molecular weight (Mw) measured according to ISO 16014-4:2003 of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is at least 250 kg/mol.

6. Heterophasic polypropylene composition according to claim 3 , wherein Mw/Mn (MWD) of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is from 3.5 to 6.0, wherein Mn is the number average molecular weight measured according to ISO 16014-4:2003 and Mw is the weight average molecular weight measured according to ISO 16014-4:2003.

7. Heterophasic polypropylene composition according to claim 3 , wherein the polypropylene matrix (M) fulfils the equation:

MFR/ XS> 25

wherein

“MFR” is the MFR 2 (230° C.) [g/10 min] of the polypropylene matrix (M) measured according to ISO 1133, and

“XS” is the amount of the xylene cold soluble fraction [wt.-%] of the polypropylene matrix (M) measured according to ISO 6427(23° C.).

8. Heterophasic polypropylene composition according to claim 3 , wherein the polypropylene matrix (M) has an MFR 2 (230° C.) measured according to ISO 1133 of more than 50 g/10 min.

9. Heterophasic polypropylene composition according to claim 3 , wherein the polypropylene matrix (M) has a xylene cold soluble fraction (XCS) measured according to according to ISO 6427(23° C.) of not more than 3.5 wt.-%.

10. Heterophasic polypropylene composition according to claim 3 , wherein:

(a) the polypropylene matrix (M) is an isotactic propylene homopolymer, and/or,

(b) the elastomeric copolymer (E) comprises monomer units derived from propylene and ethylene only.

11. Heterophasic polypropylene composition according to claim 3 , wherein the polypropylene matrix (M) and the elastomeric copolymer (E) together contribute to at least 85 wt.-% to the heterophasic polypropylene composition.

12. Articles, comprising a heterophasic polypropylene composition comprising:

73 to 98 wt.-% of a polypropylene matrix (M) being a propylene homopolymer, and,

2 to 27 wt.-% of an elastomeric copolymer (E) being dispersed in the matrix (M),

based on the polypropylene matrix (M) and the elastomeric copolymer (E)

wherein the elastomeric copolymer (E) comprises units derived from

propylene and

ethylene and/or C4 to C20 α-olefin,

and wherein further,

Mz/Mw of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is of more than 2.6, wherein Mz is the z-average molecular weight measured according to ISO 16014-4:2003 and Mw is the weight average molecular weight measured according to ISO 16014-4:2003,

the intrinsic viscosity of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is above 2.1 dl/g measured according to ISO 1628-1 (at 135° C. in decaline), and

the MFR 2 (230° C.) of the heterophasic polypropylene composition measured according to ISO 1133 is more than 25 g/10 min, and wherein the amount of propylene derived monomer units in the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is at least 58 wt.-%.

13. Process for the preparation of a heterophasic polypropylene composition comprising:

producing in a first slurry reactor and optionally in a second slurry reactor, both slurry reactors using the same polymerization conditions, a polypropylene matrix (M) using a catalyst system comprising

(i) a Ziegler-Natta procatalyst which contains a trans-esterification product of a lower alcohol and a phthalic ester,

(ii) optionally an organometallic cocatalyst and

(iii) an external donor represented by formula (III)

Si(OCH 3 ) 2 R 2 5   (III)

wherein R 5 represents a branched-alkyl group having 3 to 12 carbon atoms, or a cyclo-alkyl having 4 to 12 carbon atoms,

transferring the slurry reactor product into at least a first gas phase reactor,

producing an elastomeric copolymer (E) in the presence of the polypropylene matrix (M) and in the presence of the catalyst system in at least said first gas phase reactor,

recovering the polymer product for further processing,

wherein

73 to 98 wt.-% of a polypropylene matrix (M) being a propylene homopolymer, and,

2 to 27 wt.-% of an elastomeric copolymer (E) being dispersed in the matrix (M),

based on the polypropylene matrix (M) and the elastomeric copolymer (E)

wherein the elastomeric copolymer (E) comprises units derived from

propylene and

ethylene and/or C4 to C20 α-olefin,

and wherein further,

Mz/Mw of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is of more than 2.6, wherein Mz is the z-average molecular weight measured according to ISO 16014-4:2003 and Mw is the weight average molecular weight measured according to ISO 16014-4:2003,

the intrinsic viscosity of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is above 2.1 dl/g measured according to ISO 1628-1 (at 135° C. in decaline),

the MFR 2 (230° C.) of the heterophasic polypropylene composition measured according to ISO 1133 is more than 25 g/10 min, and wherein the amount of propylene derived monomer units in the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is at least 58 wt.-%.

14. Heterophasic polypropylene composition according to claim 3 , wherein the polypropylene matrix (M) has a xylene cold soluble fraction (XCS) measured according to according to ISO 6427(23° C.) of not more than 3.0 wt.-%.

15. Heterophasic polypropylene composition according to claim 1 , wherein the weight average molecular weight (Mw) measured according to ISO 16014-4:2003 of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is at least 250 kg/mol.

16. Heterophasic polypropylene composition according to according to claim 1 , wherein Mw/Mn (MWD) of the xylene cold soluble fraction (XCS) of the heterophasic polypropylene composition is from 3.5 to 6.0, wherein Mn is the number average molecular weight measured according to ISO 16014-4:2003 and Mw is the weight average molecular weight measured according to ISO 16014-4:2003.

17. Heterophasic polypropylene composition according to according to claim 1 , wherein the polypropylene matrix (M) fulfils the equation

MFR/XS>25

wherein

“MFR” is the MFR 2 (230° C.) [g/10 min] of the polypropylene matrix (M) measured according to ISO 1133, and

“XS” is the amount of the xylene cold soluble fraction [wt.-%] of the polypropylene matrix (M) measured according to ISO 6427 (23° C.).

18. Heterophasic polypropylene composition according to according to claim 1 , wherein the polypropylene matrix (M) has a xylene cold soluble fraction (XCS) measured according to according to ISO 6427 (23° C.) of not more than 3.5 wt.-%.