View Patent ↗The present invention relates to “grafting to” methods of modifying materials surfaces with high-density polymer brushes. A method of the present invention comprises contacting in succession or simultaneously an activated material surface, a solution of a polymeric material having a polymeric backbone with pendant reactive moieties, and a melt of brush-forming terminally-functionalized polymer chains, in order to allow a covalent bonding reaction to occur between surface and polymers, wherein upon completion of the reaction, the polymeric material forms a layer between the material surface and the brush polymer chains.
1. A method of preparing a polymer brush on a material surface comprising the steps of:
a) contacting an optionally (and preferably) activated and optionally (and preferably) functionalized material surface with:
i) a polymeric material having a polymeric backbone with pendant reactive moieties wherein said polymeric material reacts with said activated and optionally functionalized material surface to form on said surface a pre-coat layer of chemisorbed polymeric material having pendant reactive moieties for the covalent bonding of terminally-functionalized polymer chains to said pre-coat layer, or
ii) polymerizable monomers under conditions wherein said monomers form a polymeric material having a polymeric backbone with pendant reactive moieties wherein said polymeric material reacts with said activated and optionally functionalized material surface to form on said surface a pre-coat layer of chemisorbed polymeric material having pendant reactive moieties for the covalent bonding of terminally-functionalized polymer chains to said pre-coat layer;
(b) optionally removing unreacted polymeric or monomeric material;
(c) contacting the resultant pre-coat layer with terminally-functionalized polymer chains having at least one terminal functional group, wherein said terminally-functionalized polymer chains are in the form of a melt when contacted with said pre-coat layer, and wherein said at least one terminal functional group reacts with at least one pendant reactive moiety to provide for tethered polymer chains covalently bonded to said pre-coat layer of polymeric material, and optionally removing unreacted polymer chains.
2. Method according to claim 1 , wherein said polymeric material comprises at least one pendant reactive moiety per monomer.
3. Method according to claim 1 , wherein said pendant reactive moieties are carboxyl moieties, wherein said at least one terminal functional group is the amine group, and wherein said material surface is activated by corona treatment and subsequently functionalized with aminoalkylsilane.
4. Method according to claim 3 , wherein said polymeric material is a polyacrylic acid or a derivative thereof, wherein said terminally-functionalized polymer chains are 1-octadecylamine, and wherein said material surface is functionalized with 3-aminopropyltriethoxysilane.
5. Method according to claim 1 , wherein said terminally-functionalized polymer chains are polymethacrylates chains, optionally further functionalized with methyl or ethyl quaternary ammonium chloride side groups.
6. Method according to claim 1 , wherein said terminally-functionalized polymer chains are degradable polymer chains.
7. Method according to claim 6 , wherein said method further comprises the steps of providing the tethered polymer chains with a controlled release functionality, preferably by chemisorbing or physisorbing a medicament to said tethered polymer chains.
8. Method according to claim 1 , wherein said polymeric material is provided in the form of a solution in order to react with said optionally activated and optionally functionalized material surface.
9. Method according to claim 1 , wherein said polymers in said melt have a polydispersity Mw/Mn of between 1.03 and 1.1, preferably of between 1.03 and 1.08.
10. Method according to claim 1 , wherein said tethered polymer chains in said polymer brush have a polydispersity Mw/Mn of between 1.03 and 1.1, preferably of between 1.03 and 1.08, and wherein said polymer brush has a polymer density of between 0.5 nm −2 and 2 nm −2 , preferably between 0.8 nm −2 and 1.5 nm −2 .
11. A polymer brush on a material surface, said polymer brush consisting of tethered polymer chains covalently bonded to a layer of polymeric material positioned in between said tethered chains and said surface, wherein a plurality of tethered chains is bonded to a single polymer molecule of said polymeric material, and wherein said tethered chains in said polymer brush have a polydispersity Mw/Mn of between 1.03 and 1.1, preferably of between 1.03 and 1.08, and wherein said polymer brush has a polymer density of between 0.5 nm −2 and 2 nm −2 , preferably between 0.8 nm −2 and 1.5 nm −2 .
12. A polymer brush according to claim 11 , wherein said polymeric material is derived from acrylic acid.
13. A polymer brush according to claim 12 , wherein said covalent bonds between said polymeric material and said tethered chains is the amide bond.
14. A polymer brush according to claim 11 , wherein said tethered polymer chains are selected from the group consisting of hydrocarbon polymers, polyacrylates, polyethers, polyesters, polycarbonate, polysulfone, polyamides, polyimides, polyurethane, polysiloxanes, cellulose, polypeptides and derivatives, copolymers thereof.
15. A polymer brush according to claim 11 , wherein said tethered polymer chains are polymethacrylates functionalized with methyl or ethyl quaternary ammonium chloride side groups.
16. A polymer brush according to claim 11 , wherein said tethered polymer chains are degradable and adapted for controlled release of medicaments.
17. A polymer brush according to claim 16 , wherein said material surface is selected from part of a wound dressing or stent.
18. Method for producing a polymer brush according to claim 11 , comprising binding the polymeric material to a material surface to form a pre-coat layer and binding terminally-functionalized polymer chains to said pre-coat layer to form the tethered polymer chains.
19. Method according to claim 2 , wherein:
said pendant reactive moieties are carboxyl moieties, wherein said at least one terminal functional group is the amine group, and wherein said material surface is activated by corona treatment and subsequently functionalized with aminoalkylsilane;
said polymeric material is a polyacrylic acid or a derivative thereof, wherein said terminally-functionalized polymer chains are 1-octadecylamine, and wherein said material surface is functionalized with 3-aminopropyltriethoxysilane;
said terminally-functionalized polymer chains are polymethacrylates chains, optionally further functionalized with methyl or ethyl quaternary ammonium chloride side groups;
said terminally-functionalized polymer chains are degradable polymer chains;
said method further comprises the steps of providing the tethered polymer chains with a controlled release functionality, preferably by chemisorbing or physisorbing a medicament to said tethered polymer chains;
said polymeric material is provided in the form of a solution in order to react with said optionally activated and optionally functionalized material surface;
said polymers in said melt have a polydispersity Mw/Mn of between 1.03 and 1.1, preferably of between 1.03 and 1.08;
said tethered polymer chains in said polymer brush have a polydispersity Mw/Mn of between 1.03 and 1.1, preferably of between 1.03 and 1.08, and wherein said polymer brush has a polymer density of between 0.5 nm −2 and 2 nm −2 , preferably between 0.8 nm −2 and 1.5 nm −2 .
20. A polymer brush obtained by a method according to claim 19 .
21. A polymer brush according to claim 13 , wherein:
said tethered polymer chains are selected from the group consisting of hydrocarbon polymers, polyacrylates, polyethers, polyesters, polycarbonate, polysulfone, polyamides, polyimides, polyurethane, polysiloxanes, cellulose, polypeptides and derivatives, copolymers thereof;
said tethered polymer chains are degradable and adapted for controlled release of medicaments; and
said material surface is selected from part of a wound dressing or stent.
22. Method for producing a polymer brush according to claim 21 , comprising binding the polymeric material to a material surface to form a pre-coat layer and binding terminally-functionalized polymer chains to said pre-coat layer to form the tethered polymer chains.
23. A polymer brush according to claim 21 , wherein said tethered polymer chains are polymethacrylates functionalized with methyl or ethyl quaternary ammonium chloride side groups.