Gold carbon monoxide oxidation catalysts with etched substrate
Applicant discloses multifunctional, highly active oxidation catalysts and methods of making such catalysts. Such methods include providing nanoparticles comprising titanium-oxo and zinc-oxo compositions, such as crystalline anatase titania nanoparticles with zinc-oxo domains on their surfaces, and etching the nanoparticles. The method also includes depositing catalytically active gold onto the nanoparticles, by, for example, physical vapor deposition.
1. A method of making a catalyst, comprising the steps of: providing a plurality of crystalline anatase titania nanoparticles,
wherein at least some of the nanoparticles possess a multi-domain composite structure comprising at least zinc-oxo domains and titanium-oxo domains;
etching the nanoparticles with an acidic etchant so as to remove at least a portion of the zinc-oxo domains from at least some of the nanoparticles; and, depositing gold clusters of dimensions of about 0.5 nm to about 50 nm onto the etched nanoparticles.
2. The method of claim 1 , wherein the etching process preferentially removes zinc-oxo material in comparison to titanium-oxo material.
3. The method of claim 2 , wherein the etchant comprises nitric acid.
4. The method of claim 1 , further comprising the step of drying the etched nanoparticles.
5. The method of claim 1 , wherein the gold clusters are deposited via physical vapor deposition.
6. The method of claim 1 , wherein the nanoparticles comprise crystalline anatase titania nanoparticles having zinc-oxo domains on their surfaces and having a TiO2 content of about 81% and a specific surface area of about 250 m2/g
7. The method of claim 1 , further comprising the step of depositing the etched nanoparticles on a host material so as to form a catalyst system comprising a guest/host structure.
8. The method of claim 7 , further comprising the step of incorporating the catalyst system with at least one activating agent.
9. The method of claim 7 , further comprising the step of incorporating the catalyst system with at least one filtering agent.
10. The method of claim 7 , wherein the host material comprises activated carbon.
11. The method of claim 1 wherein the etched nanoparticles have a mean particle size in the range of about 3 nm to about 15 nm.
12. The method of claim 1 wherein the etched nanoparticles comprise nanoporosity.
13. The method of claim 1 wherein the etched nanoparticles are present as aggregates having a mean particle size in the range of about 0.1 μm to about 3 μm.
14. The method of claim 13 wherein the aggregates comprise nanoporosity.