Polyester woven fabric
A polyester fabric having a total cover factor of not lower than 1500 and a mass per unit area of not higher than 45 g/m 2 , wherein said polyester fabric is composed of polyester multifilament A yarns having a total fineness of not higher than 25 dtex (decitex) and a single yarn fineness of not higher than 2.0 dtex and multifilament B yarns having a total fineness of not lower than 35 dtex, wherein the arrangements of the respective yarns in the warp and weft directions are such that the yarn constitution ratio “B yarn/A yarn” is ¼ to 1/20 (number of yarns-to-number of yarns ratio) and wherein the A yarn-to-B yarn pitches are not longer than 7 mm. The polyester fabric is light in weight, high in density and flexible by using extra-fine polyester multifilaments finer as compared with the conventional polyester multifilaments and, at the same time, has a sufficient level of tear strength.
1. A bag made of a downproof fabric, said fabric consisting essentially of:
a polyester fabric having a total cover factor of not lower than 1600 and a mass per unit area of not higher than 45 g/m 2 , the fabric having been treated by calendering,
wherein said polyester fabric is composed of polyester multifilament A yarns having a total fineness of not higher than 25 dtex and a single yarn fineness of not higher than 2.0 dtex and multifilament B yarns having a total fineness of not lower than 35 dtex,
wherein the multifilament B yarn comprises polyester multifilaments and/or polyamide multifilaments,
wherein the arrangements of the respective yarns in the warp and weft directions are such that the yarn constitution ratio “B yarn/A yarn” is ¼ to 1/20, and
wherein there are 4 to 20 A yarns and then 1 B yarn, and the distance between the B yarns is not longer than 7 mm.
2. The bag according to claim 1 , wherein the B yarns are paralleled yarns.
3. The bag according to claim 1 , wherein the polyester fabric has a tear strength of not lower than 7 N in each of the warp and weft directions and an air permeability of not higher than 1.2 cc/cm 2 /sec.
4. A warmth retaining material which comprises the bag according to claim 1 and a warmth retaining mass packed in said bag.
5. The bag according to claim 2 , wherein the polyester fabric has a tear strength of not lower than 7 N in each of the warp and weft directions and an air permeability of not higher than 1.2 cc/cm 2 /sec.
6. A warmth retaining material which comprises the bag according to claim 2 and a warmth retaining mass packed in said bag.
7. The bag according to claim 1 , wherein the polyester fabric has a thickness of 0.065 mm or less.
8. The bag according to claim 1 , wherein said calendaring fills interstitial spaces in the fabric.
9. The bag according to claim 1 , wherein the fabric has a softness parameter of at least 70 mm, according to test method JIS L 1096 Bending resistance testing 6.19.4 Method D.
10. The bag according to claim 1 , wherein the fabric is treated by at least one step selected from the group consisting of scouring, waterproofing, air impermeability imparting, and dyeing.