UV curable silsesquioxane resins for nanoprint lithography
View Patent ↗Radiation-curable silsesquioxane resin materials are employed for micro- and nanolithography. The resin materials can include a radiation-curable silsesquioxane resin and a photo-initiator having low viscosity. The low viscosity of the liquid system allows imprinting with low pressure and low temperature; e.g. room temperature. The resist's dry etching resistance is increased and the cured film is more easily separated from the mask. Due to its high modulus after cure, the material allows the fabrication of micro- and nano-features having high aspect ratios while providing a high throughput. Various pattern sizes, for example, ranging from tens of microns to as small as a few nanometers, may be achieved with the UV-curable material system.
1. A stamp or mold for nanoimprint lithography comprising a cured organosiloxane resin that defines a feature having at least one dimension of greater than or equal to about 2 nanometers to less than or equal to about 100 micrometers for nanoimprint lithography, wherein the organosiloxane resin is a reaction product formed in the presence of a basic catalyst that comprises at least one silsesquioxane unit of formula (II):
—(R 2 SiO 1.5 )— (II)
wherein R 2 is at least one radiation-curable group independently selected from the group consisting of acrylate, epoxy, and vinyl ether groups;
a second unit selected from:
—(R 5 SiO 1.5 )— or —(R 1 R 5 SiO)—, wherein R 5 is a C1-C12 linear or branched alkyl group including at least one halogen heteroatom; and
at least one additional unit selected from:
—(R 1 SiO 1.5 )—; or (I)
—(SiO 2 )—; (IV)
wherein R 1 is independently selected from the group consisting of hydrogen; C1-C12 linear or branched alkyl groups; C1-C12 linear or branched alkyl groups including at least one heteroatom selected from the group consisting of nitrogen, oxygen, and combinations thereof; C1-C12 linear or branched carboxylate groups; C1-C12 linear or branched ether groups; and C6-C12 aryl groups, including phenyl groups.
2. The stamp or mold of claim 1 , wherein the radiation-curable group is curable with actinic radiation, or both thermal and actinic radiation.
3. The stamp or mold of claim 1 , wherein the organosiloxane resin comprises at least one di-functional (D) unit of formula (III) derived from a difunctional silane, R 3 R 4 SiX 2 , wherein X is a halide, alkoxyl, or acetoxy group:
—(R 3 R 4 SiO)— (III)
wherein:
R 3 and R 4 are independently selected from the group consisting of hydrogen; C1-C12 linear or branched alkyl groups; C1-C12 linear or branched alkyl groups including at least one heteroatom selected from the group consisting of nitrogen, oxygen, halogen, and combinations thereof; C1-C12 linear or branched carboxylate groups; C1-C12 linear or branched ether groups; C6-C12 aryl groups, including phenyl groups; and fluoro-containing organic groups, including fluoro-alkyl groups and fluoro-ether groups; and a radiation-curable group selected from the group consisting of acrylate, epoxy, and vinyl ether groups.
4. The stamp or mold of claim 1 , wherein the organosiloxane resin comprises at least one quadri-functional (Q) unit of formula (IV) derived from SiX 4 monomer, wherein X is a halide, alkoxyl, or acetoxy group: (IV) —(SiO 2 )—.
5. The stamp or mold of claim 1 , wherein the organosiloxane resin comprises one of the following formulas:
[R 1 SiO 3/2 ] m [R 2 SiO 3/2 ] n [R 1 R 5 SiO] p ( T R1 T R2 D R1,R5 ,m+n+p= 1);
[R 1 SiO 3/2 ] m [R 2 SiO 3/2 ] n [R 1 R 5 SiO] p [SiO 2 ] q ( T R1 T R2 D R1,R5 Q,m+n+p+q= 1);
[R 2 SiO 3/2 ] n [R 1 R 5 SiO] p [SiO 2 ] q ( T R2 D R1,R5 Q,n+p+q= 1);
[R 2 SiO 3/2 ] n [R 5 SiO 3/2 ] o [SiO 2 ] q ( T R2 T R5 Q,n+o+q= 1);
[R 1 SiO 3/2 ] m [R 2 SiO 3/2 ] n [R 5 SiO 3/2 ] o ( T R1 T R2 T R5 ,m+n+o= 1);
wherein:
R 1 , R 2 , and R 5 are as defined in claim 1 ,
m is the molar ratio of [R 1 SiO 3/2 ] unit;
n is the molar ratio of [R 2 SiO 3/2 ] unit;
p is the molar ratio of [R 1 R 5 SiO] unit;
q is the molar ratio of [SiO 2 ] unit; and
o is the molar ratio of [R 5 SiO 3/2 ] unit;
with the proviso that the sum of the molar ratios of all components in each formula is equal to 1.
6. The stamp or mold of claim 1 , wherein the organosiloxane resin comprises one of the following formulas:
[R 1 SiO 3/2 ] m [R 2 SiO 3/2 ] n [R 1 R 5 SiO] p ( T R1 T R2 D R1,R5 ,m+n+p= 1);
[R 1 SiO 3/2 ] m [R 2 SiO 3/2 ] n [R 5 SiO 3/2 ] o ( T R1 T R2 T R5 ,m+n+o= 1);
wherein:
R 1 , R 2 , and R 5 are as defined in claim 1 ,
m is the molar ratio of [R 1 SiO 3/2 ] unit;
n is the molar ratio of [R 2 SiO 3/2 ] unit;
p is the molar ratio of [R 1 R 5 SiO] unit;
and
o is the molar ratio of [R 5 SiO 3/2 ] unit;
with the proviso that the sum of molar ratios of all components in each formula is equal to 1.
7. The stamp or mold of claim 1 , wherein the cured organosiloxane resin comprises a fluoro-containing organic group, fluoro-alkyl group, or fluoro-ether group.
8. The stamp or mold of claim 1 , wherein the cured organosiloxane resin has a modulus of about 0.5 GPa to about 4.5 GPa.
9. The stamp or mold of claim 1 , wherein the organosiloxane resin is made by hydrolysis of at least one of the following units: R 1 SiX 3 , R 2 SiX 3 , R 3 R 4 SiX 2 , R 5 SiX 3 , or combinations thereof in the presence of a basic catalyst, wherein X is a halide, an alkoxy group, or an acetoxy group.
10. The stamp or mold of claim 1 , wherein the basic catalyst is selected from the group consisting of: tetramethylammonium hydroxide (TMAH) or cesium hydroxide (CsOH).
11. The stamp or mold of claim 1 , wherein the organosiloxane resin has been heat-treated and reacted with a silane compound to remove residual silanol groups.
12. The stamp or mold of claim 11 , wherein R 2 is a radiation-curable group independently selected from the group consisting of epoxy and vinyl ether groups.
13. The stamp or mold of claim 1 , wherein the cured organosiloxane resin has a molecular weight of about 1,000 g/mol to about 6,000 g/mol.
14. The stamp or mold of claim 1 , wherein the cured organosiloxane resin has a shrinkage rate of less than or equal to about 6% as compared to the organosiloxane resin prior to curing.
15. A stamp or mold for nanoimprint lithography comprising a cured organosiloxane resin that defines a feature having at least one dimension of greater than or equal to about 2 nanometers to less than or equal to about 100 micrometers for nanoimprint lithography, wherein the organosiloxane resin is a reaction product formed in the presence of a basic catalyst that comprises at least one silsesquioxane unit of formula (II):
—(R 2 SiO 1.5 )— (II)
wherein R 2 is at least one radiation-curable group independently selected from the group consisting of acrylate, epoxy, and vinyl ether groups;
a second unit selected from:
—(R 5 SiO 1.5 )— or —(R 1 R 5 SiO)—, wherein R 5 is a C1-C12 linear or branched alkyl group including at least one fluorine heteroatom; and
at least one additional unit selected from:
—(R 1 SiO 1.5 )—; or (I)
—(SiO 2 )—; (IV)
wherein R 1 is independently selected from the group consisting of hydrogen; C1-C12 linear or branched alkyl groups; C1-C12 linear or branched alkyl groups including at least one heteroatom selected from the group consisting of nitrogen, oxygen, and combinations thereof; C1-C12 linear or branched carboxylate groups; C1-C12 linear or branched ether groups; and C6-C12 aryl groups, including phenyl groups.
16. The stamp or mold of claim 15 , wherein the cured organosiloxane resin has a molecular weight of about 1,000 g/mol to about 6,000 g/mol and the cured organosiloxane resin has a shrinkage rate of less than or equal to about 6% as compared to the organosiloxane resin prior to curing.
17. A nano-patterned article formed from nanoimprint lithography comprising a patterned surface defining at least one mechanically imprinted feature having at least one dimension of greater than or equal to about 2 nanometers to less than or equal to about 100 micrometers, wherein the nano-patterned article comprises a cured organosiloxane resin that is a reaction product formed in the presence of a basic catalyst that comprises at least one silsesquioxane unit of formula (II):
—(R 2 SiO 1.5 )— (II)
wherein R 2 is at least one radiation-curable group independently selected from the group consisting of acrylate, epoxy, and vinyl ether groups;
a second unit selected from:
—(R 5 SiO 1.5 )— or —(R 1 R 5 SiO)—, wherein R 5 is a C1-C12 linear or branched alkyl group including at least one fluorine heteroatom; and
at least one additional unit selected from:
—(R 1 SiO 1.5 )—; or (I)
—(SiO 2 )—; (IV)
wherein R 1 is independently selected from the group consisting of hydrogen; C1-C12 linear or branched alkyl groups; C1-C12 linear or branched alkyl groups including at least one heteroatom selected from the group consisting of nitrogen, oxygen, and combinations thereof; C1-C12 linear or branched carboxylate groups; C1-C12 linear or branched ether groups; and C6-C12 aryl groups, including phenyl groups.
18. The nano-patterned article of claim 17 , wherein the cured organosiloxane resin has a molecular weight of about 1,000 g/mol to about 6,000 g/mol and the cured organosiloxane resin has a shrinkage rate of less than or equal to about 6% as compared to the organosiloxane resin prior to curing.