Flexible polyurethane foams prepared using modified vegetable oil-based polyols
A flexible polyurethane foam prepared by reacting, in the presence of a blowing agent, a polyisocyanate with an active hydrogen-containing composition that includes a modified vegetable oil-based polyol. The foams exhibit good load-bearing properties, relatively high sag factors, and/or good color retention upon exposure to light.
1. A flexible polyurethane foam comprising the reaction product, in the presence of a blowing agent, of:
(a) a polyisocyanate; and
(b) an active hydrogen-containing composition comprising (i) 1 to 40 parts by weight of a modified vegetable oil-based polyol per 100 parts of active hydrogen-containing composition, and (ii) a polyether polyols,
wherein the foam is flexible and has a load efficiency number of at least 7 Newtons/part modified vegetable oil-based polyol, an wherein the modified vegetable oil-based polyol is prepared by a process comprising:
(a) providing an epoxidized vegetable oil; and
(b) combining the epoxidized vegetable oil with an alcohol and a catalytic amount of fluoroboric acid to form the modified vegetable oil-based polyol.
2. A flexible polyurethane foam according to claim 1 wherein the epoxidized vegetable oil is a partially epoxidized vegetable oil, and the modified vegetable oil-based polyol includes double bonds.
3. A flexible polyurethane foam comprising the reaction product, in the presence of a blowing agent, of:
(a) a polyisocyanate; and
(b) an active hydrogen-containing composition comprising (i) 1 to 40 parts by weight of a modified vegetable oil-based polyol per 100 parts of active hydrogen-containing composition, and (ii) a polyether polyol,
wherein the foam is flexible and has a load efficiency number of at least 7 Newtons/part modified vegetable oil-based polyol and wherein the foam, upon exposure to light at ambient conditions for a period of 6 weeks in the absence of an ultraviolet stabilizer, has a color characterized by an (L) value of at least 70 units and a (b) value of no greater than 25 units, and wherein the modified vegetable oil-based polyol is prepared by a process comprising:
(a) providing an epoxidized vegetable oil; and
(b) combining the epoxidized vegetable oil with an alcohol and a catalytic amount of fluoroboric acid to form the modified vegetable oil-based polyol.
4. A flexible polyurethane foam according to claim 3 wherein the epoxidized vegetable oil is a partially epoxidized vegetable oil, and the modified vegetable oil-based polyol includes double bonds.
5. A flexible polyurethane foam comprising the reaction product, in the presence of a blowing agent, of:
(a) a polyisocyanate; and
(b) an active hydrogen-containing composition comprising (i) 1 to 40 parts by weight of a modified vegetable oil-based polyol per 100 parts of active hydrogen-containing composition, and (ii) a polyether polyol,
wherein the foam is flexible and has a load efficiency number of at least 7 Newtons/part modified vegetable oil-based polyol and wherein the foam, as manufactured, has an (L) value of at least 70 units and a (b) value of no greater than 25 units, and wherein, upon exposure to light under ambient conditions for a period of 6 weeks in the absence of an ultraviolet stabilizer, the (L) value does not change by more than 14 units and the (b) value does not change by more than 14 units, and wherein the modified vegetable oil-based polyol is prepared by a process comprising:
(a) providing an epoxidized vegetable oil; and
(b) combining the epoxidized vegetable oil with an alcohol and a catalytic amount of fluoroboric acid to form the modified vegetable oil-based polyol.
6. A flexible polyurethane foam according to claim 5 wherein the epoxidized vegetable oil is a partially epoxidized vegetable oil, and the modified vegetable oil-based polyol includes double bonds.
7. A seat component comprising a flexible polyurethane foam, the polyurethane foam comprising the reaction product, in the presence of a blowing agent, of:
(a) a polyisocyanate; and
(b) an active hydrogen-containing composition comprising (i) 1 to 40 parts by weight of a modified vegetable oil-based polyol per 100 parts of active hydrogen-containing composition, and (ii) a polyether polyol,
wherein the foam is flexible and has a load efficiency number of at least 7 Newtons/part modified vegetable oil-based polyols, and wherein the modified vegetable oil-based polyol is prepared by a process comprising:
(a) providing an epoxidized vegetable oil; and
(b) combining the epoxidized vegetable oil with an alcohol and a catalytic amount of fluoroboric acid to form the modified vegetable oil-based polyol.
8. A flexible polyurethane foam comprising the reaction product, in the presence of a blowing agent, of:
(a) a polyisocyanate and
(b) an active hydrogen-containing composition comprising 1 to 40 parts by weight of a soybean oil-based polyol per 100 parts of active hydrogen-containing composition and a polyether polyol,
wherein the modified soybean oil-based polyol is prepared by a process comprising:
(A) providing an epoxidized soybean oil and combining the epoxidized soybean oil with an alcohol and a catalytic amount of fluoroboric acid to form the modified soybean oil-based polyol;
(B) reacting soybean oil with carbon monoxide and hydrogen in the presence of a Group VIII metal catalyst to form a hydroformylated soybean oil, and hydrogenating the hydroformylated soybean oil to form the modified soybean oil-based polyol; or
(C) reacting a vegetable oil with carbon monoxide and hydrogen in the presence of a Group VIII metal catalyst to form a hydroformylated vegetable oil, hydrogenating the hydroformylated vegetable oil to form a polyol, and combining the polyol with an epoxidized vegetable oil and a catalytic amount of fluoroboric acid to form the modified vegetable oil-based polyol,
wherein the foam is flexible and has a load efficiency number of at least 7 Newtons/part modified soybean oil-based polyol.
9. A flexible polyurethane foam according to claim 8 wherein the epoxidized vegetable oil is a partially epoxidized vegetable oil, and the modified vegetable oil-based polyol includes double bonds.
10. A seat component comprising a flexible polyurethane foam, the polyurethane foam comprising the reaction product, in the presence of a blowing agent, of:
(a) a polyisocyanate and
(b) an active hydrogen-containing composition comprising 1 to 40 parts by weight of a modified soybean oil-based polyol per 100 parts of active hydrogen-containing composition and a polyether polyol,
wherein the modified soybean oil-based polyol is prepared by a process comprising:
(A) providing an epoxidized soybean oil, and combining the epoxidized soybean oil with a mixture comprising an alcohol and a catalytic amount of fluoroboric acid to form the modified soybean oil-based polyol;
(B) reacting soybean oil with carbon monoxide and hydrogen in the presence of a Group VIII metal catalyst to form a hydroformylated soybean oil, and hydrogenating the hydroformylated soybean oil to form the modified soybean oil-based polyol; or
(C) reacting a vegetable oil with carbon monoxide and hydrogen in the presence of a Group VIII metal catalyst to form a hydroformylated vegetable oil, hydrogenating the hydroformylated vegetable oil to form a polyol, and combining the polyol with an epoxidized vegetable oil and a catalytic amount of fluoroboric acid to form the modified vegetable oil-based polyol,
wherein the foam is flexible and has a load efficiency number of at least 7 Newtons/part modified soybean oil-based polyol.
11. A flexible polyurethane foam according to claim 10 wherein the epoxidized vegetable oil is a partially epoxidized vegetable oil, and the modified vegetable oil-based polyol includes double bonds.